【摘要】：介紹了幾種常見的納米纖維制備方法,并對他們進(jìn)行了比較分析。提出一種改進(jìn)型離心轉(zhuǎn)子制備納米纖維裝置,該裝置具有可連續(xù)供料、收集距離可調(diào)、可適應(yīng)紡絲盤或針筒等特點。分析了離心轉(zhuǎn)子法制備納米纖維的工作原理,并對納米纖維制備過程中噴絲頭處的聚合物射流進(jìn)行運動分析。運用三維設(shè)計平臺SolidWorks進(jìn)行了離心轉(zhuǎn)子納米纖維制備裝置的三維設(shè)計、裝配與仿真,以及所有零件加工圖的繪制,進(jìn)行了裝置的試制與裝配調(diào)試,構(gòu)建了基本的實驗平臺,并進(jìn)行了初步納米紡絲實驗。
[Abstract]:This paper introduces several common preparation methods of nanofibers and makes a comparative analysis of them.An improved centrifugal rotor device for preparing nanofibers is proposed.The device has the characteristics of continuous feeding,adjustable collection distance and adaptability to spinning disk or needle barrel.The working principle of preparing nanofibers by centrifugal rotor method is analyzed. In the process of fiber preparation, the polymer jet at the spinneret head was analyzed. The three-dimensional design platform SolidWorks was used to design, assemble and simulate the centrifugal rotor nanofiber preparation device, and draw the processing drawings of all parts. The preliminary nanoscale spinning experiments were carried out.
【作者單位】： 武漢紡織大學(xué)機(jī)械工程與自動化學(xué)院;湖北數(shù)字化紡織裝備重點實驗室;迪肯大學(xué)前沿材料學(xué)院;
【基金】：湖北省科技支撐計劃對外科技合作類項目(2014BHE010)
【分類號】：TB383.1;TQ340.6

【相似文獻(xiàn)】

相關(guān)博士學(xué)位論文 前8條

1 任勃;鎳鈷基氧化物納米纖維的靜電紡絲法制備及電化學(xué)性能研究[D];哈爾濱工程大學(xué);2014年

2 劉方;納米顆粒改性環(huán)氧樹脂及其復(fù)合材料力學(xué)性能研究[D];哈爾濱工程大學(xué);2014年

3 邵韋;稀土摻雜氟化物多層核殼納米晶上轉(zhuǎn)換和量子剪裁的研究[D];哈爾濱工業(yè)大學(xué);2017年

4 李大龍;介孔磷灰石基納米藥物控制釋放體系的構(gòu)建與生物學(xué)評價[D];哈爾濱工業(yè)大學(xué);2017年

5 楊桂欣;幾種納米功能材料的合成及成像、腫瘤治療性能研究[D];哈爾濱工程大學(xué);2015年

6 仲崇娜;核殼結(jié)構(gòu)上轉(zhuǎn)換稀土化合物納米晶的合成、發(fā)光性能及抗腫瘤研究[D];哈爾濱工程大學(xué);2014年

7 平浩梁;納米氧化鈣碳酸化反應(yīng)性能對甲烷蒸汽重整制氫的強(qiáng)化作用[D];浙江大學(xué);2017年

8 劉洪辰;β淀粉樣蛋白聚集的聚合物納米抑制劑的設(shè)計合成和作用[D];天津大學(xué);2016年

相關(guān)碩士學(xué)位論文 前9條

1 閆貴花;靜電紡制備聚丙烯腈/納米纖維素基多孔碳材料及電學(xué)性能研究[D];鄭州大學(xué);2017年

2 張路f，

本文編號：2211326