本文關(guān)鍵詞： 硝化棉 抗靜電 溶劑-非溶劑法 導(dǎo)電填料 發(fā)射藥　出處：《火炸藥學(xué)報(bào)》2016年01期 　論文類型：期刊論文

【摘要】：以硝化棉和導(dǎo)電填料為原料,采用溶劑-非溶劑法制備了抗靜電硝化棉復(fù)合材料。通過(guò)掃描電子顯微鏡、體積表面電阻測(cè)定儀、非接觸式靜電壓測(cè)試儀、熱分析儀表征了抗靜電硝化棉復(fù)合材料的微觀形貌、抗靜電性能及熱分解性能。結(jié)果表明,導(dǎo)電填料質(zhì)量分?jǐn)?shù)為0.6%的抗靜電硝化棉復(fù)合材料內(nèi)部導(dǎo)電網(wǎng)絡(luò)分布均勻、完整,體積電阻率和表面電阻率分別為1.02×109Ω·m和4.66×1010Ω,較硝化棉分別降低5個(gè)數(shù)量級(jí)和3個(gè)數(shù)量級(jí),達(dá)到GJB2527-1995彈藥防靜電要求,且制備過(guò)程中靜電電位為0.20kV,較硝化棉降低77.8%,顯示了良好的抗靜電性能;其表觀分解熱為259.4J/g,較硝化棉提高81.4J/g。
[Abstract]:Using nitrocellulose and conductive filler as raw materials, antistatic nitrocellulose composites were prepared by solvent-non-solvent method. The microcosmic morphology, antistatic property and thermal decomposition property of antistatic nitrified cotton composite were characterized by thermal analyzer. The results showed that the conductive network of antistatic nitrocellulose composite with conductive filler content of 0.6% was uniform and complete. The volume resistivity and surface resistivity are 1.02 脳 10 ~ 9 惟 路m and 4.66 脳 10 ~ 10 惟, respectively, which are 5 orders of magnitude and 3 orders of magnitude lower than those of nitrided cotton respectively. The electrostatic potential is 0.20 kV, which is 77.8% lower than that of nitrified cotton, showing good antistatic properties, and its apparent decomposition heat is 259.4 J / g, which is 81.4 J / g higher than that of nitrocellulose.
【作者單位】： 四川省非金屬?gòu)?fù)合與功能材料重點(diǎn)實(shí)驗(yàn)室西南科技大學(xué);瀘州北方化學(xué)工業(yè)有限公司;
【基金】：四川省非金屬?gòu)?fù)合與功能材料重點(diǎn)實(shí)驗(yàn)室開放基金資助項(xiàng)目(No.13zxFk21)
【分類號(hào)】：TQ560.1

【相似文獻(xiàn)】

中國(guó)期刊全文數(shù)據(jù)庫(kù) 前3條

1 尚雁;葉志虎;王友兵;李亞南;王伯周;;HNS-Ⅳ的制備及粒徑、形貌控制[J];含能材料;2011年03期

2 孫娥;丁安偉;張麗;;荊芥內(nèi)酯聚乳酸乙醇酸納米粒的制備及其穩(wěn)定性研究[J];中草藥;2007年12期

3 ;[J];;年期

中國(guó)碩士學(xué)位論文全文數(shù)據(jù)庫(kù) 前1條

1 徐牛牛;不同形態(tài)RDX的制備及其形態(tài)特征對(duì)熱性能影響[D];南京理工大學(xué);2013年

，

本文編號(hào)：1545344