【摘要】：采用簡(jiǎn)化預(yù)處理輔助化學(xué)鍍法制備了WC-Ni復(fù)合粉體,結(jié)合壓制燒結(jié)法獲得了不同Ni含量的WC-Ni復(fù)合材料。通過FESEM,EDS和XRD檢測(cè)手段分析了原始WC粉、WC-Ni復(fù)合粉體形貌和WC-Ni復(fù)合材料的表面形貌和斷口特征。研究了不同Ni含量對(duì)WC-Ni復(fù)合材料組織和性能的影響規(guī)律。結(jié)果表明,Ni顆粒均勻包覆在WC粉體表面,WC-Ni復(fù)合材料具有細(xì)小均勻的晶粒分布;隨著Ni含量的增加,WC-Ni復(fù)合材料的抗彎強(qiáng)度增加,硬度基本保持不變,斷口形貌表現(xiàn)出穿晶斷裂特征。
[Abstract]:WC-Ni composite powders were prepared by simplified pretreatment assisted electroless plating, and WC-Ni composites with different Ni content were obtained by pressing sintering method. FESEM was used. The original WC powder was analyzed by EDS and XRD. The morphology of WC-Ni composite powder and the surface morphology and fracture characteristics of WC-Ni composite were studied. The effect of Ni content on the microstructure and properties of WC-Ni composite was studied. The uniform coating of Ni particles on WC powder surface shows fine and uniform grain distribution of WC-Ni composite. With the increase of Ni content, the flexural strength of WC-Ni composites increases, the hardness remains unchanged, and the fracture morphology shows transgranular fracture characteristics.
【作者單位】： 合肥工業(yè)大學(xué);有色金屬與加工技術(shù)國(guó)家地方聯(lián)合工程研究中心;臺(tái)州學(xué)院;
【基金】：National Magnetic Confinement Fusion Program(2014GB121001) Fund Project of Zhejiang Provincial Key Laboratory for Cutting Tools(ZD201301)
【分類號(hào)】：TB33;TF125
【正文快照】： Tungsten carbides are widely employed in tribologicalfields because of their good performance and good wearresistance[1 5].For cemented carbides,the properties canbe modified by the presence of a second phase[6].Cobalt,as the second phase,shows good wet

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 崔升;沈曉冬;肖蘇;高志強(qiáng);;化學(xué)鍍法制備金屬銅包覆納米碳化硅[J];粉末冶金技術(shù);2008年04期

2 周超蘭;張高科;甘慧慧;;化學(xué)鍍法制備鈷包覆碳化硅復(fù)合粉末的研究[J];武漢理工大學(xué)學(xué)報(bào);2011年07期

3 曾高峰;史蕾;徐恒泳;;用化學(xué)鍍法制備Pd/Ag膜時(shí)膜厚和組成的控制[J];催化學(xué)報(bào);2009年12期

4 梁勝德,朱時(shí)珍,趙振波,鐘家湘;化學(xué)鍍法制備金屬/陶瓷復(fù)合粉體的特點(diǎn)及應(yīng)用[J];材料導(dǎo)報(bào);1996年05期

5 陳慕容;賀躍輝;江W，

本文編號(hào)：1490884