本文選題：秘色瓷　切入點：越窯　出處：《故宮博物院院刊》2017年06期

【摘要】：為揭示秘色瓷胎釉成分特征及其與普通越窯青瓷之間的異同,并探討越窯青瓷制釉技術(shù)的時代特征,本文采用X射線熒光能譜儀(EDXRF)對慈溪上林湖后司岙和荷花芯窯址出土的青瓷標(biāo)本進行了無損測試。結(jié)果表明:(1)后司岙窯址秘色瓷的胎體元素組成與普通越窯青瓷無明顯的差異,即二者均采用當(dāng)?shù)氐拇墒现铺?(2)晚唐和五代秘色瓷釉的元素組成與同時期普通越窯青瓷也無明顯差異,其獨特的釉色與其采用瓷質(zhì)匣缽的燒制工藝有關(guān);(3)晚唐至五代時期越窯青瓷釉料配方可能發(fā)生了重大改變,即由早期的瓷石加草木灰的二元配方變成瓷石加草木灰、石灰石的三元配方。(4)晚唐至五代秘色瓷以及五代耀州窯青瓷、北宋汝官窯、南宋官窯以及龍泉南宋青瓷均將釉中氧化鈣的含量嚴(yán)格控制在10%?14%范圍之內(nèi),即各個窯口的制釉技術(shù)是非常類似的。
[Abstract]:In order to reveal the characteristics of the composition of the inner glaze and the similarities and differences between the inner glaze of the secret porcelain and that of the ordinary Yue kiln celadon, and to probe into the age characteristics of the glazing technology of the Yue kiln celadon, In this paper, the samples of celadon unearthed from Houshiao and Lotus core kiln sites in Shanglin Lake, Cixi, were tested by X-ray fluorescence energy spectrometer (EDXRFF). The results showed that there was no significant difference between the composition of the matrix elements of the cryptic porcelain in Housi'ao kiln site and that in the common Yue kiln celadon, and the results showed that there was no significant difference between the composition of the matrix elements and that of the common Yue kiln celadon. That is to say, the element composition of the porcelain glaze of the late Tang Dynasty and the five dynasties was not significantly different from that of the common Yue kiln celadon in the same period. Its unique glaze color is related to the firing process of porcelain sagger) during the late Tang Dynasty to the five dynasties, the prescription of Yue kiln celadon glaze may have undergone a major change, that is, from the early binary formula of porcelain stone and plant ash to porcelain stone and plant ash. The ternary formula of limestone. Yaozhou Kiln celadon from late Tang to five dynasties, North Song RU Guan Kiln, Southern Song official Kiln and Longquan Southern Song celadon all strictly control the content of calcium oxide in glaze at 10? Within 14% of the range, that is, each kiln mouth glaze making technology is very similar.
【作者單位】： 故宮博物院;浙江省文物考古研究所;
【基金】：國家自然科學(xué)基金(項目編號:51402054)資助
【分類號】：K876.3

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 周麗麗;關(guān)于“秘色瓷”兩個問題的討論[J];文博;1995年06期

2 陳克倫;秘色瓷及其相關(guān)問題[J];文博;1995年06期

3 趙宏;秘色瓷續(xù)考[J];景德鎮(zhèn)陶瓷;1997年02期

4 劉浩;;秘色瓷[J];對外大傳播;2000年07期

5 ;也說秘色瓷[J];收藏界;2002年08期

6 郭丹英;秘色瓷新考[J];東南文化;2003年01期

7 鄭嘉勵;“秘色瓷”說[J];東方博物;2005年01期

8 李剛;;“秘色瓷”之秘再探[J];東方博物;2005年04期

9 馮彬妮;;精美絕倫秘色瓷[J];大眾文藝(理論);2008年09期

10 王宇雯;;當(dāng)審美與市場一同返璞歸真——高古秘色瓷現(xiàn)階段投資看點[J];藝術(shù)市場;2009年03期

相關(guān)重要報紙文章 前7條

1 西北大學(xué) 張璐;法門寺秘色瓷的佛教美學(xué)[N];光明日報;2011年

2 法門寺博物館研究員 姜捷;千峰翠色:唐葵口圈足秘色瓷碗[N];人民日報;2013年

3 關(guān)山;“千峰翠色”的秘瓷[N];安徽日報;2005年

4 浙江省博物館研究員 趙幼強;奪得千峰翠色來[N];美術(shù)報;2013年

5 本報駐陜西記者 趙建蘭;法門寺琉璃器皿的背后[N];中國文化報;2014年

6 孫玉潔;六萬余件中國珍寶待價而沽[N];中國藝術(shù)報;2004年

7 劉剛 冬君;瓷器里的江山[N];中國經(jīng)營報;2012年

相關(guān)碩士學(xué)位論文 前2條

1 張璐;陜西扶風(fēng)法門寺秘色瓷視覺文化研究[D];西北大學(xué);2009年

2 趙雯;滲透在越窯秘色瓷中的雕塑藝術(shù)[D];景德鎮(zhèn)陶瓷學(xué)院;2011年

，

本文編號：1655037