【摘要】：氯離子引起的鋼筋銹蝕是影響鋼筋混凝土結構耐久性的主要原因之一�；贔ick第二定律,推導了PHC(Prestress high concrete)管樁氯離子擴散的解析解,并對PHC管樁設計壽命進行了預測,且考慮了離心分層和溫度作用對PHC管樁設計壽命的影響。結果表明:離心分層和溫度對PHC管樁中氯離子擴散影響較大,而初始氯離子含量對其影響較小。綜合考慮離心分層和溫度影響,確定了海工環(huán)境中PHC管樁的設計要求,即對于要求服役壽命大于50a的工程,壁厚應大于100mm,且砂漿層不宜大于10mm,而對于服役壽命要求大于100a的工程,應選用壁厚150mm的PHC管樁,且砂漿層宜小于30mm。
[Abstract]:The corrosion of steel bar caused by chloride ion is one of the main reasons that affect the durability of reinforced concrete structure. Based on the second law of Fick, the analytical solution of chloride diffusion of PHC (Prestress high concrete) pipe pile is derived, and the design life of PHC pipe pile is predicted, and the influence of centrifugal stratification and temperature on the design life of PHC pipe pile is considered. The results show that the effect of centrifugal stratification and temperature on the chloride diffusion in PHC pipe pile is greater, but the initial chlorine ion content has little effect on it. Considering the influence of centrifugal stratification and temperature, the design requirements of PHC pipe pile in marine engineering environment are determined, that is, for projects whose service life is more than 50 years. The wall thickness should be more than 100mm, and the mortar layer should not be more than 10mm. For the project whose service life is more than 100a, the PHC pipe pile with wall thickness 150mm should be selected, and the mortar layer should be less than 30mm.
【作者單位】： 同濟大學地下建筑與工程系;同濟大學巖土及地下工程教育部重點實驗室;
【基金】：國家自然科學基金項目(51178341)資助項目
【分類號】：TV223;TU473.13

【參考文獻】

相關期刊論文 前10條

1 余紅發(fā);孫偉;;混凝土氯離子擴散理論模型[J];東南大學學報(自然科學版);2006年S2期

2 汪冬冬;王成啟;時蓓玲;張造揚;;大管樁現(xiàn)場取樣分析與耐久性研究[J];中國港灣建設;2008年01期

3 余紅發(fā),孫偉,鄢良慧,麻海燕;混凝土使用壽命預測方法的研究I——理論模型[J];硅酸鹽學報;2002年06期

4 邵偉;李鏡培;岳著文;;氯離子侵蝕混凝土管樁壽命預測理論模型[J];硅酸鹽學報;2013年05期

5 田冠飛;安雪暉;;鋼筋存在對氯離子擴散阻滯影響的有限元分析[J];混凝土;2006年05期

6 嚴志隆;陸酉教;仲以林;高仁輝;;PHC管樁混凝土耐久性[J];混凝土與水泥制品;2008年06期

7 陳正;楊綠峰;馮慶革;劉鴻亮;王q，

本文編號：2239449