【摘要】：以烯丙基聚氧乙烯醚(APEG)和甲基烯丙基聚氧乙烯醚(TPEG)復合單體與丙烯酸(AA)和烯丙基磺酸鈉(SAS)為原料,在硫代硫酸鈉(Na2S2O3)和復合引發(fā)劑體系的作用下,采用一步共聚法制備復合型聚羧酸高性能減水劑。從反應溫度對減水劑分散性能的影響入手,從熱動力學角度對單體活性的激發(fā),反應體系聚合速率、引發(fā)劑的分解速率等進行了深入的研究,并結(jié)合紅外光譜分析探討了不同溫度下合成減水劑的分子結(jié)構(gòu)與減水劑性能的相關(guān)性。
[Abstract]:The composite monomers of allyl polyoxyethylene ether (APEG) and methyl allyl polyoxyethylene ether (TPEG) were used as raw materials with acrylic acid (AA) and sodium allyl sulfonate (SAS) as raw materials under the action of sodium thiosulfate (Na2S2O3) and complex initiator system. Compound polycarboxylic acid superplasticizer was prepared by one-step copolymerization. Starting with the effect of reaction temperature on the dispersion of water reducer, the activation of monomer activity, the polymerization rate of reaction system and the decomposition rate of initiator were studied in detail from the point of view of thermokinetics. The correlation between the molecular structure and the properties of the water reducer at different temperatures was discussed by infrared spectroscopy.
【作者單位】： 武漢科技大學城市建設(shè)學院;華中科技大學化學與化工學院;福州新奧化工有限公司;
【基金】：湖北省自然科學基金資助項目(2010CDZ062)
【分類號】：TU528.042.2

【參考文獻】

相關(guān)期刊論文 前4條

1 朱琳俐;馮恩娟;徐正華;嚴生;;聚醚接枝聚羧酸系高效減水劑合成[J];南京工業(yè)大學學報(自然科學版);2010年01期

2 蘇偉偉;唐建華;;三元共聚醚類聚羧酸減水劑的合成及性能研究[J];四川化工;2011年04期

3 馬保國;胡家兵;譚洪波;;兩種醚類聚羧酸減水劑的合成和應用[J];新型建筑材料;2012年05期

4 袁莉弟;謝吉民;丁繼華;陳景文;;聚醚型聚羧酸減水劑的側(cè)鏈結(jié)構(gòu)對其性能的影響[J];新型建筑材料;2012年06期

【共引文獻】

相關(guān)期刊論文 前10條

1 黃玉華;陳錢寶;汪志勇;;高保坍低引氣型聚羧酸超塑化劑P(APEG-AA-UASO)的結(jié)構(gòu)及性能研究[J];廣東化工;2011年06期

2 劉娟;張兵;;聚羧酸系高效減水劑合成工藝優(yōu)化研究[J];長春工程學院學報(自然科學版);2013年02期

3 陳寶t，

本文編號：2170475