本文關(guān)鍵詞： 缺口件 相對應(yīng)力梯度 體積法 疲勞壽命預(yù)測　出處：《應(yīng)用力學學報》2016年04期 　論文類型：期刊論文

【摘要】：針對Mod.9Cr-1Mo鋼不同缺口半徑下的多軸疲勞試驗結(jié)果進行模擬計算,采用體積法進行疲勞壽命預(yù)測,并與等效應(yīng)變法的預(yù)測結(jié)果進行了對比。模擬結(jié)果表明,各路徑下缺口根部應(yīng)力集中程度隨缺口半徑減小而更為明顯,最大應(yīng)力集中程度達3.45。等效應(yīng)變法給出的疲勞壽命預(yù)測結(jié)果隨著缺口半徑的減小而偏于保守,保守量高達90倍。為克服等效應(yīng)變法給出的偏于保守的結(jié)果,基于剪應(yīng)力隨距缺口根部距離的變化趨勢進行有效距離的計算,采用體積法進行壽命預(yù)測,94.1%的預(yù)測結(jié)果位于2倍分散帶內(nèi)。
[Abstract]:The multiaxial fatigue test results of Mod.9Cr-1Mo steel with different notched radii are simulated and calculated. The fatigue life is predicted by volume method, and compared with the prediction results of equal-effect variation method. The simulation results show that, The stress concentration at the root of the notch is more obvious with the decrease of the notch radius, and the maximum stress concentration is 3.45. The prediction results of fatigue life obtained by the equal-effect variation method are conservative with the decrease of the notch radius. The conservative quantity is up to 90 times. In order to overcome the conservative results given by the equal-effect variation method, the effective distance is calculated based on the trend of shear stress changing with the distance from the root of the notch. The prediction results of 94.1% of the lifetime predicted by volume method are in the dispersion band of 2 times.
【作者單位】： 湖南理工學院機械工程學院;沈陽化工大學能源與動力工程學院;
【基金】：國家自然科學基金(11102119) 國家重點基礎(chǔ)研究發(fā)展計劃(2011CB706504) 湖南省自然科學基金(13JJ6067)
【分類號】：O346.2

【相似文獻】

相關(guān)期刊論文 前1條

1 郭慶超，何明民，韓其為;控制體積法在二維潮流計算中的應(yīng)用[J];水動力學研究與進展(A輯);1995年06期

相關(guān)會議論文 前1條

1 李政;金先龍;陳向東;;復(fù)雜氣囊展開過程動態(tài)模擬方法的研究[A];慶祝中國力學學會成立50周年暨中國力學學會學術(shù)大會’2007論文摘要集（下）[C];2007年

相關(guān)碩士學位論文 前2條

1 侯冶;高階譜體積方法計算精度研究[D];哈爾濱工程大學;2008年

2 方安石;一種有限體積邊界嵌入法的研究及應(yīng)用[D];南京航空航天大學;2011年

，

本文編號：1506724