本文選題：膨潤土 + 超聲離心��； 參考：《非金屬礦》2017年03期

【摘要】：以四川三臺、廣西田東、新疆夏子街3個產(chǎn)地的膨潤土為原料進行鈉化提純實驗,對比重力沉降與超聲離心兩種不同鈉化提純工藝效果;探索離心轉速、離心時間、鈉化劑用量對鈉化提純效果的影響,通過物化性能的測試,比較提純前后陽離子交換容量(CEC)、膨脹容、膠質(zhì)價、吸藍量。采用X-射線熒光、X-射線衍射儀分析原礦及提純樣品的化學成分和物相組成。結果表明,超聲離心可以提高提純效果,并且提純后物化性能有大幅提升。
[Abstract]:Using bentonite from three producing areas of Santai, Guangxi Tian Dong and Xiazijie, Xinjiang as raw material, sodium purification experiments were carried out to compare the effects of gravity sedimentation and ultrasonic centrifugation, to explore centrifugation speed and time. The effect of the amount of sodium agent on the purification effect of sodium was studied. The cationic exchange capacity (CEC), swelling capacity, colloidal value and blue absorption amount were compared before and after purification by physical and chemical tests. The chemical composition and phase composition of raw ore and purified samples were analyzed by X ray fluorescence X ray diffractometer. The results show that ultrasonic centrifugation can improve the purification effect, and the physical and chemical properties of the purification can be greatly improved.
【作者單位】： 固體廢物資源化教育部重點實驗室;西南科技大學礦物材料及應用研究所;
【基金】：國家自然科學基金(41372052)
【分類號】：TD97

【相似文獻】

中國期刊全文數(shù)據(jù)庫 前10條

1 羅太安,劉曉東;廣豐膨潤土鈉化改型研究[J];非金屬礦;2004年03期

2 蔣沖,曹佳宏,石云良;桃源膨潤土鈉化改型研究[J];礦冶工程;2004年06期

3 李彩霞;任瑞晨;董慶國;王秀蘭;;某膨潤土鈉化改性性能試驗研究[J];遼寧工程技術大學學報(自然科學版);2009年04期

4 徐光亮;;鄂州膨潤土濕法提純及鈉化改型試驗研究[J];中國非金屬礦工業(yè)導刊;2010年06期

5 林濤;任建曉;殷學風;;膨潤土的鈉化工藝研究[J];陜西科技大學學報(自然科學版);2013年03期

6 胡茂焱 ,鄭秀華;膨潤土的鈉化及最優(yōu)加堿量的確定[J];非金屬礦;1991年03期

7 李永倫;王力;;鈣基蒙脫土的鈉化改型[J];礦產(chǎn)保護與利用;2007年02期

8 馮輝霞;張國宏;李春雷;邵亮;趙陽;張婷;邱建輝;邱明;;平?jīng)鲡}基膨潤土干法鈉化工藝研究[J];非金屬礦;2007年04期

9 李翠珍;任廣元;高建衛(wèi);;有機鈉鹽對膨潤土的鈉化研究[J];礦產(chǎn)保護與利用;2007年04期

10 鐘春龍;涂逢樟;吳|，

本文編號：1969058