【摘要】：正GCr18Mo鋼制軸承經(jīng)貝氏體等溫淬火后,可以獲得比馬氏體淬回火更優(yōu)越的力學(xué)性能,被廣泛應(yīng)用于一些要求承受較高的沖擊載荷的工作環(huán)境。某批次GCr18Mo鋼制圓柱軸承外圈,外徑尺寸為250 mm,經(jīng)下貝氏體等溫淬火后,在產(chǎn)品的檢驗(yàn)過(guò)程中,發(fā)現(xiàn)該批次產(chǎn)品的外徑尺寸漲縮規(guī)律出現(xiàn)反常:外圈留量漲大正常約為0.60~0.80 mm,而該批產(chǎn)品外徑的漲大留量偏小。為了查清產(chǎn)生這一現(xiàn)象的原因,對(duì)熱處理加
[Abstract]:After isothermal quenching of GCr18Mo steel bearings, the mechanical properties are superior to those of martensite quenching and tempering, and are widely used in some working environments which require higher impact loads. The outer ring of a batch of GCr18Mo steel cylindrical bearings with an outer diameter of 250 mm, after isothermal quenching of lower bainite, It is found that the outer diameter of the batch product is abnormal: the normal value of the increase of the outer ring diameter is about 0.60 ~ 0.80 mm, while the increase of the outer diameter of the batch product is relatively small. In order to find out the causes of this phenomenon, heat treatment is added
【作者單位】： 洛陽(yáng)LYC軸承有限公司航空精密軸承國(guó)家重點(diǎn)實(shí)驗(yàn)室;
【分類號(hào)】：TH133.3;TG155.3

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 張華;客車軸承貝氏體等溫淬火生產(chǎn)線[J];金屬熱處理;2004年09期

2 仲部;;球墨鑄鐵的貝氏體等溫淬火以獲取高強(qiáng)度及韌性[J];鑄造技術(shù);1982年04期

3 費(fèi)明節(jié);貝氏體等溫淬火生產(chǎn)線在軸承套圈上的應(yīng)用[J];金屬熱處理;2001年10期

4 張?jiān)銎?劉耀中,樊志強(qiáng);貝氏體等溫淬火及其在軸承上的應(yīng)用[J];金屬熱處理學(xué)報(bào);2002年01期

5 盧國(guó)輝;黃惠平;揭曉華;楊建宏;陳基偉;;提高貝氏體等溫淬火連續(xù)生產(chǎn)線上馬弗罐使用壽命的方法[J];熱加工工藝;2008年16期

6 侯振剛;;77752G軸承貝氏體等溫淬火冷卻工藝[J];金屬加工(熱加工);2012年13期

7 陳洵;;國(guó)外期刊文摘[J];金屬熱處理;1985年11期

8 倪洪濤;貝氏體等溫淬火在模具處理中的應(yīng)用[J];模具工業(yè);1993年11期

9 任忍奎,姜振雄;白口鑄鐵的熱軋與貝氏體等溫淬火[J];金屬熱處理;1995年05期

10 燕來(lái)生,趙金蘭;碳鋼貝氏體等溫淬火對(duì)組織和性能的影響[J];內(nèi)蒙古工業(yè)大學(xué)學(xué)報(bào)(自然科學(xué)版);1999年03期

相關(guān)碩士學(xué)位論文 前1條

1 周志云;新型中碳軸承鋼貝氏體等溫淬火工藝及回火穩(wěn)定性研究[D];山東大學(xué);2012年

，

本文編號(hào)：2414231