The pack cementation was employed to improve the electrochemical corrosion resistance of 304 stainless steel via CeO2-Cr modified Ti coatings. Continuous coatings were formed on 304 stainless steel surface by this method. A series of electrochemical experiments were carried out to investigate the corrosion resistance of 304 stainless steel, Ti coating and CeO2-Cr/Ti coatings. The sample surface was investigated by scanning electron microscopy（SEM）. The phases of sample surface were detected by X... 

【文章來源】：Journal of Rare Earths. 2015,33(10)EISCICSCD

【文章頁數(shù)】：7 頁

【文章目錄】：
1 Experimental
    1.1 Materials
    1.2 Preparation of Ce O2-Cr/Ti coatings
    1.3 Electrochemical corrosion resistance tests
2 Results and discussion
    2.1 Microstructural characterization
    2.2 Electrochemical corrosion resistance in 3.5%Na Cl solution
3 Conclusions


【參考文獻(xiàn)】：
期刊論文
[1]304不銹鋼表面Mo合金化改性層組織結(jié)構(gòu)及耐磨性研究[J]. 劉成松,秦林,李翠玲,尹研,賈亞斌,郭麗麗.  表面技術(shù). 2014(05)
[2]TiO2薄膜的制備及其對304不銹鋼防腐性能的研究[J]. 吳震弘,汪洋,馮佩,毛麗婷.  浙江理工大學(xué)學(xué)報(bào). 2014(03)
[3]Vapor phase codeposition of Cr and Si on Nb-base in situ composites by pack cementation process[J]. Bifei Yuan,Yang Li,Min Qiao,Chungen Zhou.  Progress in Natural Science:Materials International. 2013(02)
[4]滲鉻P110鋼在CO2飽和模擬油田采出液中的耐蝕性[J]. 林乃明,謝發(fā)勤,吳向清,田偉.  沈陽工業(yè)大學(xué)學(xué)報(bào). 2012(01)
[5]Influence of process parameters on thickness and wear resistance of rare earth modified chromium coatings on P110 steel synthesized by pack cementation[J]. 林乃明,謝發(fā)勤,吳向清,田偉.  Journal of Rare Earths. 2011(04)
[6]Microstructures and wear resistance of chromium coatings on P110 steel fabricated by pack cementation[J]. 林乃明,謝發(fā)勤,周俊,鐘濤,吳向清,田偉.  Journal of Central South University of Technology. 2010(06)
[7]油氣田CO2腐蝕的防護(hù)技術(shù)研究[J]. 熊穎,陳大鈞.  全面腐蝕控制. 2007(04)
[8]稀土元素對鋼滲鉻層組織與性能的影響[J]. 林祥豐,張瑞容.  金屬熱處理學(xué)報(bào). 1995(03)



本文編號：3446312