【摘要】：采用金相顯微鏡、力學(xué)性能測試、加工性能測試等手段,觀測和測試了不同合金化處理與不同蠕化效果的兩種蠕墨鑄鐵的顯微組織、拉伸強(qiáng)度、布氏硬度、基體顯微硬度以及切削抗力。分析了兩種蠕墨鑄鐵的切削加工性能和力學(xué)性能與顯微組織之間的關(guān)系。研究結(jié)果發(fā)現(xiàn):在蠕墨鑄鐵的石墨含量相同的條件下,蠕化率低的蠕墨鑄鐵中珠光體組織多,抗拉強(qiáng)度和硬度較高;蠕化率高的蠕墨鑄鐵顯微組織更趨于均勻,切削抗力小,切削加工性能好。
[Abstract]:The microstructure, tensile strength and Brinell hardness of two kinds of vermicular graphite cast iron with different alloying treatment and different vermicular effect were observed and tested by means of metallographic microscope, mechanical property test and processing property test. Matrix microhardness and cutting resistance. The relationship between machinability, mechanical properties and microstructure of two kinds of vermicular graphite cast iron was analyzed. The results show that under the condition of the same graphite content in vermicular graphite cast iron, the pearlite structure, tensile strength and hardness of vermicular graphite cast iron with low vermicular rate are more than those of vermicular graphite cast iron. The microstructure of vermicular graphite cast iron with high compactness tends to be more uniform, the cutting resistance is small and the machinability is good.
【作者單位】： 河南科技大學(xué)材料科學(xué)與工程學(xué)院;河南科技大學(xué)有色金屬共性技術(shù)河南省協(xié)同創(chuàng)新中心;洛陽理工學(xué)院機(jī)電工程系;
【基金】：國家自然科學(xué)基金項(xiàng)目(51201061) 河南省科技創(chuàng)新人才計(jì)劃基金項(xiàng)目(144200510009) 長江學(xué)者創(chuàng)新團(tuán)隊(duì)發(fā)展計(jì)劃基金項(xiàng)目(IRT1234) 河南基礎(chǔ)與前沿技術(shù)研究基金項(xiàng)目(11230041002)
【分類號】：TG143

【參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 段春爭;李園園;李國和;;高速切削溫度場模擬仿真研究現(xiàn)狀[J];機(jī)械制造;2007年07期

2 劉治軍;熊毅;任鳳章;高廣東;趙廣華;;氣缸套用灰鑄鐵等溫淬火后的組織與性能[J];河南科技大學(xué)學(xué)報(bào)(自然科學(xué)版);2013年03期

3 金育蓉;任小中;李彬;;兩種不同合金組元的灰鑄鐵切削加工性能[J];河南科技大學(xué)學(xué)報(bào)(自然科學(xué)版);2014年01期

4 李大勇;石德全;王利華;;Monitoring of Quality of Vermicular Cast Iron from the Front of the Furnace[J];Tsinghua Science and Technology;2008年02期

5 萬仁芳;;汽車蠕墨鑄鐵件的應(yīng)用與發(fā)展[J];現(xiàn)代鑄鐵;2006年01期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 張s，

本文編號：2345064