【摘要】：利用金相顯微鏡分析7A04鋁合金半固態(tài)與鑄態(tài)組織,對(duì)半固態(tài)與鑄態(tài)7A04鋁合金進(jìn)行極化曲線與阻抗譜電化學(xué)測試分析,通過中性鹽霧實(shí)驗(yàn)對(duì)比分析二者的質(zhì)量損失率、腐蝕面積率和腐蝕坑深度,并采用激光共聚焦顯微鏡分析腐蝕形貌差異。結(jié)果表明:半固態(tài)初生α(Al)晶粒細(xì)小圓整,半固態(tài)試樣的耐腐蝕性能優(yōu)于鑄態(tài)試樣的,半固態(tài)試樣腐蝕質(zhì)量損失率較低,半固態(tài)試樣的蝕坑平均深度及最大深度均小于鑄態(tài)試樣的。半固態(tài)工藝可顯著提高7A04鋁合金的耐腐蝕性能。
[Abstract]:The semi-solid and as-cast microstructure of 7A04 aluminum alloy was analyzed by metallographic microscope, and the polarization curve and impedance spectrum of semi-solid and as-cast 7A04 aluminum alloy were analyzed by polarization curve and impedance spectroscopy. The mass loss rate of the two alloys was compared and analyzed by neutral salt spray test. The corrosion area rate and the depth of the corrosion pit were analyzed by laser confocal microscope. The results show that the primary 偽 (Al) grains of semisolid samples are fine and round, the corrosion resistance of semi-solid samples is better than that of as-cast samples, and the loss rate of corrosion quality of semi-solid samples is lower than that of as-cast samples. The average depth and maximum depth of the etch pit of the semi-solid sample are lower than that of the as-cast specimen. The corrosion resistance of 7A04 aluminum alloy can be improved by semi-solid process.
【作者單位】： 四川理工學(xué)院工程實(shí)踐中心;四川理工學(xué)院機(jī)械工程學(xué)院;四川大西洋焊接材料股份有限公司;西南交通大學(xué)材料科學(xué)與工程學(xué)院;
【基金】：國家自然科學(xué)基金資助項(xiàng)目(51275432)
【分類號(hào)】：TG146.21

【參考文獻(xiàn)】

相關(guān)期刊論文 前2條

1 上官曉峰;董大軍;黃淑菊;樓瑞祥;;鑄造鋁合金A356抗應(yīng)力腐蝕性能研究[J];鑄造技術(shù);2008年03期

2 ;Microstructure characteristics and solidification behavior of wrought aluminum alloy 2024 rheo-diecast with self-inoculation method[J];China Foundry;2012年04期

【共引文獻(xiàn)】

相關(guān)期刊論文 前6條

1 胡勇;倪旭武;胡強(qiáng);;二次加熱對(duì)Al-0.3Ce合金半固態(tài)組織的影響[J];兵器材料科學(xué)與工程;2015年03期

2 李晨;孟祥琦;劉暢;許金泉;;ZL101鋁合金應(yīng)力腐蝕特性研究[J];力學(xué)季刊;2011年03期

3 劉興海;張繼淵;李元東;周宏偉;張心龍;;流變擠壓鑄造2024鋁合金輪轂組織及其典型缺陷分析[J];特種鑄造及有色合金;2013年11期

4 李元東;劉興海;張心龍;周宏偉;;變形鋁合金半固態(tài)近凈成形研究進(jìn)展[J];特種鑄造及有色合金;2014年05期

5 朱艷麗;趙君文;李微;朱振宇;戴光澤;張鯤;;電磁攪拌對(duì)7A04鋁合金大體積半固態(tài)漿料組織的影響[J];中國有色金屬學(xué)報(bào);2014年11期

6 耿秀明;高海燕;;自動(dòng)化列車用6005A-T6鋁合金焊接接頭的微觀組織與力學(xué)性能[J];鑄造技術(shù);2015年10期

相關(guān)博士學(xué)位論文 前1條

1 林沖;高鐵含量過共晶鋁硅合金的超聲處理及流變特性[D];華中科技大學(xué);2014年

相關(guān)碩士學(xué)位論文 前6條

1 陳永炳;Mg_2Si/Al復(fù)合材料半固態(tài)擠壓組織及磨損性的研究[D];吉林大學(xué);2013年

2 馬德清;LSPWES法中半固態(tài)組織演化的元胞自動(dòng)機(jī)模擬[D];太原科技大學(xué);2014年

3 朱艷麗;變形鋁合金大體積半固態(tài)漿料電磁攪拌制備工藝的研究[D];西南交通大學(xué);2014年

4 劉興海;變形鋁合金自孕育凝固過程與擠壓鑄造研究[D];蘭州理工大學(xué);2014年

5 徐佳;氣流攪拌制備AZ91-Ca阻燃鎂合金半固態(tài)漿料及機(jī)理研究[D];上海交通大學(xué);2014年

6 諶慶春;多重鋁—稀土共晶反應(yīng)細(xì)化半固態(tài)A356鋁合金初生α相的研究[D];江西理工大學(xué);2014年

【二級(jí)參考文獻(xiàn)】

相關(guān)期刊論文 前9條

1 董杰,路貴民,任棲鋒,崔建忠;液相線鑄造法非枝晶半固態(tài)組織形成機(jī)理探討[J];金屬學(xué)報(bào);2002年02期

2 李元東;楊建;馬穎;;自孕育半固態(tài)制漿技術(shù)的研究[J];特種鑄造及有色合金;2010年03期

3 李培躍;熊柏青;張永安;李志輝;王國軍;朱寶宏;;2D70耐熱鋁合金鑄態(tài)組織研究[J];稀有金屬;2011年01期

4 郭洪民;楊湘杰;張萌;;Microstructure characteristics and mechanical properties of rheoformed wrought aluminum alloy 2024[J];Transactions of Nonferrous Metals Society of China;2008年03期

5 王順成;李元元;陳維平;鄭小平;;Microstructure evolution of semi-solid 2024 alloy during two-step reheating process[J];Transactions of Nonferrous Metals Society of China;2008年04期

6 郭洪民;羅學(xué)泉;章愛生;楊湘杰;;Isothermal coarsening of primary particles during rheocasting[J];Transactions of Nonferrous Metals Society of China;2010年08期

7 R.CANYOOK;S.PETSUT;S.WISUTMETHA NGOON;M.C.FLEMINGS;J.WANNASIN;;Evolution of microstructure in semi-solid slurries of rheocast aluminum alloy[J];Transactions of Nonferrous Metals Society of China;2010年09期

8 李元東;楊建;馬穎;曲俊峰;張鵬;;自孕育劑參數(shù)對(duì)自孕育鑄造法制備AM60鎂合金半固態(tài)漿料的影響(Ⅱ)[J];中國有色金屬學(xué)報(bào);2010年11期

9 董大軍;上官曉峰;;鑄造鋁合金A356平面斷裂韌度K_(IC)的研究[J];鑄造;2007年05期

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 吳浩青,張敏敏;鋼樣在磷酸鈉溶液中氯離子存在的極化曲線與腐蝕曲線[J];化工學(xué)報(bào);1957年01期

2 華保定;;測定極化曲線所用儀器裝置[J];化學(xué)通報(bào);1957年09期

3 ;極化曲線的測定[J];天津電鍍;1979年08期

4 黃作華;;極化曲線相交法在評(píng)選制鹽耐蝕低合金鋼中的應(yīng)用[J];井礦鹽技術(shù);1981年03期

5 王鎧;顏天祿;;極化曲線測定儀與土的腐蝕性測定[J];勘察科學(xué)技術(shù);1992年06期

6 姚能富;鍍鐵的研究[J];西安公路交通大學(xué)學(xué)報(bào);1994年04期

7 劉振江;張衛(wèi)國;;極化曲線在氯堿工業(yè)的應(yīng)用[J];氯堿工業(yè);2009年05期

8 吳忠利;張鳳珍;謝春福;;電鍍液極化曲線的測定(2)[J];包裝工程;1980年02期

9 劉屏;許昌淦;;鈦合金中相的電化學(xué)行為[J];金屬學(xué)報(bào);1989年04期

10 黃彥良,侯保榮,馬士德,張經(jīng)磊;消除穩(wěn)態(tài)極化曲線測量中介質(zhì)電阻影響的一種實(shí)驗(yàn)技術(shù)[J];中國腐蝕與防護(hù)學(xué)報(bào);1997年02期

相關(guān)會(huì)議論文 前4條

1 鐘福新;;表面活性劑對(duì)氫在鉻電極上極化曲線的影響[A];第九屆全國化學(xué)工藝學(xué)術(shù)年會(huì)論文集[C];2005年

2 袁國偉;于新偉;吳培金;吳國祥;;六種無氰鍍銅絡(luò)合物溶液的極化曲線研究[A];2004年全國電子電鍍學(xué)術(shù)研討會(huì)論文集[C];2004年

3 陳火平;羅序燕;李東林;李勛;;線性電位掃描測定酸性光亮鍍錫溶液極化曲線[A];2002年全國電子電鍍年會(huì)論文集[C];2002年

4 張豐;尹旭東;佟昊霖;薛致遠(yuǎn);陳洪源;王維斌;劉玲莉;;極化曲線在管道陰極保護(hù)檢測和數(shù)值模擬中的應(yīng)用[A];中國腐蝕電化學(xué)及測試方法專業(yè)委員會(huì)2012學(xué)術(shù)年會(huì)論文集[C];2012年

相關(guān)碩士學(xué)位論文 前6條

1 任乃媛;導(dǎo)電聚苯胺的腐蝕防護(hù)性能研究[D];太原理工大學(xué);2006年

2 劉長利;兩種典型介質(zhì)中P110鋼的腐蝕行為研究[D];東北石油大學(xué);2011年

3 牛紹蕊;不銹鋼的電化學(xué)腐蝕性能研究[D];蘭州理工大學(xué);2010年

4 周海波;Sb和Mn對(duì)Zn腐蝕的影響[D];沈陽理工大學(xué);2009年

5 林中楠;鐵合金在流動(dòng)海水中的腐蝕行為研究[D];大連理工大學(xué);2009年

6 孫克磊;管內(nèi)陰極保護(hù)邊界元法的程序設(shè)計(jì)及其數(shù)值實(shí)驗(yàn)[D];大連理工大學(xué);2013年

，

本文編號(hào)：2323125