【摘要】：研究低溫(77K)多向鍛造鋯-4合金累積應(yīng)變?yōu)?.48,2.96,4.44和5.91時的力學(xué)性能和組織演變。通過萬能拉伸測試和維氏硬度實驗測得多向鍛造合金的力學(xué)性能。相對于原始合金,當(dāng)鋯-4合金變形的累積變形為5.91時,其極限抗拉強度從474MPa提高到717MPa,維氏硬度從HV 190提高到HV 238。然而,由于鋯-4合金的低應(yīng)變硬化,其延展性顯著降低(18%~3.5%)。變形合金強度和硬度的提高是因為多向鍛造引起的晶粒尺寸效應(yīng)和高的位錯密度。采用光學(xué)顯微鏡和透射電鏡表征變形試樣的顯微組織演化。當(dāng)累積應(yīng)變?yōu)?.91時,經(jīng)12次多向鍛造后合金的微觀組織演化主要是超細晶的形成,其平均晶粒尺寸為150~250nm。
[Abstract]:The mechanical properties and microstructure evolution of the multi - directionally forged zirconium - 4 alloy at low temperature ( 77K ) were investigated . The mechanical properties and microstructure evolution of multi - directionally forged alloys were measured by universal tensile test and Vickers hardness test .
【作者單位】： Department
【基金】：BRNS,Bombay for their financial grant to this work through grant No.BRN-577-MMD
【分類號】：TG319;TG146.414

【參考文獻】

相關(guān)期刊論文 前1條

1 ;Effects of Strain Rate and Deformation Temperature on Microstructures and Hardness in Plastically Deformed Pure Aluminum[J];Journal of Materials Science & Technology;2011年01期

【共引文獻】

相關(guān)期刊論文 前10條

1 徐宏海;閻紅娟;李新民;;刀具材料深冷處理研究現(xiàn)狀及發(fā)展趨勢[J];材料導(dǎo)報;2008年S2期

2 劉嘎;王伯健;師曉莉;白鶴;徐萍;;冷拉珠光體鋼絲的加工硬化及組織性能演變研究現(xiàn)狀[J];材料導(dǎo)報;2008年S2期

3 許曉嫦;張孜昭;胡楠;;變形程度對強變形Al-4%Cu合金退火組織性能的影響[J];材料科學(xué)與工藝;2011年02期

4 李曉;李萍;王成;張倩倩;;基于SPD法顆粒增強鋁基復(fù)合材料研究綜述[J];粉末冶金工業(yè);2011年01期

5 劉潤;周蕾;王軍麗;;異步疊軋制備超細晶材料的研究進展[J];材料導(dǎo)報;2013年01期

6 史昆玉;沈濤;陳春浩;薛麗紅;嚴有為;;高能球磨制備Cu-Cr納米晶粉末[J];粉末冶金材料科學(xué)與工程;2013年04期

7 王苗;楊延清;羅賢;;超細晶鈦合金的制備及性能研究現(xiàn)狀[J];材料導(dǎo)報;2013年13期

8 于影霞;何柏林;;鎂合金焊接接頭表面自納米化及其疲勞性能研究現(xiàn)狀與展望[J];材料導(dǎo)報;2013年17期

9 吳遠志;嚴紅革;朱素琴;陳吉華;劉安民;劉先蘭;;Mg-Zn-Zr合金高應(yīng)變速率多向鍛造組織演變及力學(xué)性能[J];材料研究學(xué)報;2014年02期

10 劉曉燕;趙西成;楊西榮;張凱;解晨;;應(yīng)變速率對室溫下90°等通道轉(zhuǎn)角擠壓變形工業(yè)純鈦拉伸性能的影響[J];機械工程材料;2013年08期

相關(guān)會議論文 前2條

1 于振濤;麻西群;余森;張明華;韓建業(yè);劉春潮;;生物醫(yī)用鈦合金的微納化加工技術(shù)及最新進展[A];第十四屆全國鈦及鈦合金學(xué)術(shù)交流會論文集（下冊）[C];2010年

2 Zhen Zhang;Manping Liu;Yingda Yu;P，

本文編號：2130135