本文選題：退火 + 碳化物　； 參考：《材料熱處理學報》2015年03期

【摘要】：采用掃描電鏡觀察H13鋼不同退火條件退火過程中殘留碳化物及退火組織中碳化物形態(tài)與分布特征,利用圖像處理軟件定量分析了碳化物數(shù)量、體積分數(shù)及大小,并研究了不同退火條件對其相應的回火態(tài)力學性能的影響。結果表明,H13鋼緩慢冷卻退火,選擇Ac1~Ac3溫度區(qū)間短時保溫,可獲得均勻分布的細小球狀殘留碳化物,在退火時即使冷卻速度較快也可獲得球狀碳化物均勻分布的退火組織,并保持較好的力學性能。
[Abstract]:The morphology and distribution characteristics of carbides in the residual carbide and annealed microstructure of H13 steel during annealing are observed by scanning electron microscope. The quantity, volume fraction and size of carbides are quantitatively analyzed by image processing software, and the effects of different annealing conditions on the mechanical properties of their corresponding tempering states are studied. The results show that H13 steel is used as a result. The uniform distribution of fine spheroidal residual carbides can be obtained by the slow cooling annealing and short heat preservation in the Ac1~Ac3 temperature range. The uniform distribution of spheroidal carbides can be obtained, and the better mechanical properties are maintained even if the cooling rate is faster in annealing.
【作者單位】： 北京科技大學新材料技術研究院;北京科技大學新金屬材料國家重點實驗室;
【分類號】：TG156.2;TG142.1

【參考文獻】

相關期刊論文 前10條

1 惠衛(wèi)軍,于同仁,蘇世懷,董瀚,翁宇慶;中碳鋼球化退火行為和力學性能的研究[J];鋼鐵;2005年09期

2 劉宗昌,李文學,孫立新,邵淑艷;H13等工模具鋼退火軟化新工藝[J];國外金屬熱處理;2000年01期

3 崔];中國模具鋼現(xiàn)狀及發(fā)展(Ⅰ)[J];機械工程材料;2001年01期

4 胡明,韓季平;殘留碳化物在等溫球化處理中的作用[J];佳木斯工學院學報;1994年03期

5 鄒安全,鄧芬燕,鄧沛然;等溫球化退火對H13鋼組織和性能的影響[J];金屬熱處理;2003年08期

6 陸明和;田玉新;蔡海燕;殷光虹;;高溫均勻化退火對H13鋼芯棒帶狀偏析和沖擊性能的影響[J];金屬熱處理;2010年08期

7 周健;馬黨參;張才明;康愛軍;李向陽;陳再枝;;不同退火工藝對H13鋼組織和力學性能的影響[J];金屬熱處理;2012年05期

8 王明;馬黨參;劉振天;周健;遲宏宵;代建清;;Nb對芯棒用H13鋼偏析、液析碳化物及力學性能的影響[J];金屬學報;2014年03期

9 章為夷;球化處理中殘留碳化物的作用[J];熱加工工藝;1992年04期

10 任慧平，李文學，，劉宗昌，王玉峰;H13鋼軟化退火工藝的研究[J];熱加工工藝;1996年06期

【共引文獻】

相關期刊論文 前10條

1 劉濤;楊王s

本文編號：2085046