本文選題：失效 + 閥桿　； 參考：《熱加工工藝》2015年24期

【摘要】：對閥桿進(jìn)行宏觀檢查、金相顯微組織觀察、化學(xué)成分分析、硬度測試試驗和拉伸試驗,結(jié)果表明:該閥桿因為同時受到交變應(yīng)力和附加彎曲應(yīng)力的共同作用,在閥桿外表面處產(chǎn)生微裂紋,微裂紋逐漸擴展,致使閥桿的有效承載面積逐步縮小,直至發(fā)生斷裂。閥桿斷裂的主要原因是:閥桿的硬度偏高,強度偏低,力學(xué)性能不符合要求,而且長期在高應(yīng)力的交替作用下導(dǎo)致其發(fā)生疲勞斷裂。
[Abstract]:Macroscopical inspection, metallographic microstructure observation, chemical composition analysis, hardness test and tensile test show that the stem is subjected to both alternating stress and additional bending stress at the same time. Microcracks appear on the outer surface of the stem, and the microcracks expand gradually, which results in the effective bearing area of the stem gradually shrinking until fracture occurs. The main reason of stem fracture is that the valve stem has high hardness and low strength, and its mechanical properties do not meet the requirements, and the fatigue fracture occurs under the alternating action of high stress for a long time.
【作者單位】： 龍巖學(xué)院物理與機電工程學(xué)院;
【分類號】：TG115

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 孟繁增;;閥桿氮化事故分析[J];機械工人;1989年11期

2 張明友;;柴油機排氣閥桿斷裂失效研究[J];武漢工學(xué)院學(xué)報;1992年03期

3 李妙珍;張葵東;;閥桿與閥頭的焊接問題[J];石家莊職業(yè)技術(shù)學(xué)院學(xué)報;2006年04期

4 冷啟霜;;某電廠閥桿斷裂原因分析[J];機械工程師;2010年08期

5 王勇;季華建;文佳卉;陳海;;壓縮機電動閥閥桿斷裂原因分析[J];理化檢驗(物理分冊);2013年04期

6 李澤民,嘉趙賓;氣閥閥桿簡易倒角裝置[J];機械工人.冷加工;1991年12期

7 戴樂陽;林少芬;陳清林;段振;;排氣閥桿早期斷裂失效分析[J];熱加工工藝;2010年22期

8 楊昱;閻保秋;;細(xì)長閥桿熱處理淬火的工裝設(shè)計[J];金屬加工(熱加工);2014年15期

9 矯永臣;;閥桿與方頭處斷裂原因及處理[J];金屬加工(熱加工);2012年12期

10 劉永樣;;黃銅閥頂和不銹鋼閥桿的氧—乙炔焰釬焊[J];焊接;1976年06期

相關(guān)會議論文 前2條

1 王領(lǐng);呂鵬飛;郭宏偉;阿爾達(dá)克;;新疆油田公司某天然氣處理站閥桿斷裂分析[A];2011年全國機械行業(yè)可靠性技術(shù)學(xué)術(shù)交流會暨第四屆可靠性工程分會第三次全體委員大會論文集[C];2011年

2 倪兆榮;李志章;;輸氣管道閥門閥桿及閥套螺紋失效分析及磨損機理研究[A];第九次全國熱處理大會論文集（一）[C];2007年

，

本文編號：1917889