本文選題：激光技術(shù) + 激光立體成形��； 參考：《中國激光》2015年01期

【摘要】：以TC4鈦合金激光立體成形件及鍛件為研究對象,采用不同熱處理制度對TC4鈦合金激光立體成形件進行處理得到不同的熱處理組織,并采用超聲波無損檢測方式獲得超聲波縱波聲速和衰減系數(shù),明晰超聲參量和顯微組織的相互作用機理。結(jié)果表明,不同的顯微組織具有不同的超聲波縱波聲速和衰減系數(shù);相比超聲波縱波聲速而言,衰減系數(shù)對TC4鈦合金激光立體成形顯微組織的變化更為靈敏。
[Abstract]:Taking TC4 titanium alloy laser solid forming parts and forgings as research objects, different heat treatment systems were used to treat TC4 titanium alloy laser solid forming parts and different heat treatment structures were obtained. The ultrasonic longitudinal wave velocity and attenuation coefficient are obtained by ultrasonic nondestructive testing, and the interaction mechanism between ultrasonic parameters and microstructure is clarified. The results show that different microstructures have different ultrasonic longitudinal wave velocities and attenuation coefficients, and the attenuation coefficients are more sensitive to the changes of laser forming microstructure of TC4 titanium alloys than those of ultrasonic longitudinal wave velocities.
【作者單位】： 西北工業(yè)大學凝固技術(shù)國家重點實驗室;南昌航空大學輕合金加工科學與技術(shù)國防重點學科實驗室;陜西工業(yè)職業(yè)技術(shù)學院;西安熱工院有限公司;
【基金】：國家自然科學基金(51323008) 國家863計劃(2013AA031103)
【分類號】：TG146.23;TG115.285

【參考文獻】

相關(guān)期刊論文 前1條

1 張霜銀;林鑫;陳靜;黃衛(wèi)東;;熱處理對激光成形TC4合金組織及性能的影響[J];稀有金屬材料與工程;2007年07期

【共引文獻】

相關(guān)期刊論文 前10條

1 鐘玉;屈金山;陳文靜;潘全喜;;TC4鈦合金電子束焊接頭性能研究[J];焊接;2007年10期

2 何勝春;張?zhí)飩};;TC17鈦合金慣性摩擦焊接頭組織特征分析[J];焊接;2008年04期

3 洪志強;李萍;薛克敏;張青;;鈦合金高溫變形流變應(yīng)力的預測[J];合肥工業(yè)大學學報(自然科學版);2007年08期

4 高永輝;李重河;國子明;龐威;魯雄剛;丁偉中;鐘慶東;;TiNi合金熔煉的耐火材料研究[J];過程工程學報;2010年S1期

5 吳巍;高洪明;吳林;;細晶粒鈦合金粗晶區(qū)組織及接頭力學性能分析[J];焊接學報;2008年01期

6 吳巍;高洪明;程廣福;吳林;;細晶粒鈦合金熱影響區(qū)晶粒長大規(guī)律[J];焊接學報;2008年10期

7 周水亮;陶軍;郭德倫;;細晶粒鈦合金GTAW焊縫成形性能分析[J];焊接學報;2009年07期

8 周水亮;陶軍;杜欲曉;郭德倫;;細晶粒鈦合金薄板TIG焊溫度場分析[J];焊接學報;2010年12期

9 王錦林;甘章華;陳義明;肖建中;;不同冷卻速度對Ti-6Al-4V鈦合金熱模擬試樣組織的影響[J];焊接學報;2011年08期

10 劉紅;洪賀;范s，

本文編號：1849915