本文選題：X管線鋼 + 偏析　； 參考：《材料熱處理學(xué)報》2015年04期

【摘要】：通過LIBS-OPA-100原位分析儀、掃描電鏡(SEM)、透射電子顯微鏡(TEM)等方法,從顯微組織、硬度、偏析元素3方面研究了X65管線鋼中心偏析帶馬奧島(M/A)組元對氫致裂紋性能的影響,偏析與硬度以及偏析與氫致裂紋(HIC)之間的關(guān)系。結(jié)果表明:X65管線鋼中C、Mn、S、Si元素在中心偏析后形成硬度較高的帶狀組織是導(dǎo)致抗HIC性能不合格的主要原因;顯著的中心偏析馬奧島、鐵素體帶狀組織和大尺寸的相顆粒析出不利于抗HIC性能;帶狀的馬奧島組織是氫原子的聚集場所,是導(dǎo)致氫致裂紋萌生與擴展的源頭。
[Abstract]:By means of LIBS-OPA-100 in-situ analyzer, scanning electron microscope (SEM), transmission electron microscope (TEM) and so on, the effect of M-1 / A- component in central segregation zone of X65 pipeline steel on the properties of hydrogen-induced crack was studied from three aspects: microstructure, hardness and segregation element. The relationship between segregation and hardness and the relationship between segregation and hydrogen induced crack cracking (HIC). The results show that the formation of high hardness banded structure in the C _ (mn) Si element in the w _ X65 pipeline steel after central segregation is the main cause of the failure of the resistance to HIC, and the significant central segregation of Mayo Island, The precipitation of ferrite banded structure and large size phase particles is not conducive to the resistance to HIC, and the banded Mao island structure is the gathering place of hydrogen atoms, which is the source of the initiation and propagation of hydrogen-induced cracks.
【作者單位】： 昆明理工大學(xué)材料科學(xué)與工程學(xué)院;鋼鐵研究總院工程用鋼研究所;珠江鋼管有限公司;
【基金】：國家科技支撐計劃(2011BAE25B00,2011BAE25B03)
【分類號】：TG142.1

【參考文獻】

相關(guān)期刊論文 前3條

1 李吶,李晨光,湯智濤,崔邛;抗H_2S腐蝕管線管的開發(fā)[J];鋼管;2005年05期

2 李云濤;杜則裕;孫孌芬;陶勇寅;;高強度管線鋼的抗氫致裂紋性能[J];鋼鐵研究學(xué)報;2008年12期

3 甘春瑾;董文玲;夏崇博;;影響管線鋼氫致開裂敏感性的因素分析[J];河南冶金;2009年05期

【共引文獻】

相關(guān)期刊論文 前10條

1 王寶軍;王文俊;林均品;;Fe_3Si和316不銹鋼在工業(yè)鋅液中的腐蝕機制[J];鞍鋼技術(shù);2006年01期

2 杜迎,朱衛(wèi)良,管光寶;集成電路可靠性試驗——鹽霧技術(shù)研究[J];半導(dǎo)體技術(shù);2004年09期

3 王建軍;宋武林;郭連貴;謝長生;曾大文;;金屬納米粒子氧化機理研究進展[J];兵工學(xué)報;2006年06期

4 李志林,陳濤,曾致，

本文編號：1822454