【摘要】：為提高CoCrM合金的耐磨性,延長其使用壽命,采用磁控濺射法在其表面制備了厚度為1.89μm、分別摻W元素和摻Ti元素的2種DLC膜層。摩擦磨損實(shí)驗(yàn)測得未鍍膜層、鍍Ti-DLC膜層以及鍍W-DLC膜層的CoCrMo合金的磨損率分別是15.25×10~(-6),0.76×10~(-6)和0.19×10~(-6)mm~3·m~(-1)·N~(-1)。結(jié)果說明:鍍膜后基體的耐磨性顯著提高;鍍W-DLC的試樣比鍍Ti-DLC的試樣更耐摩。拉曼分析表明,鍍膜試樣因在摩擦過程中表層膜層發(fā)生了部分石墨化,所以表現(xiàn)出了優(yōu)異的耐磨性。
[Abstract]:In order to improve the wear resistance of CoCrM alloy and prolong its service life, two kinds of DLC films with thickness of 1.89 渭 m and doping of W and Ti were prepared on the surface by magnetron sputtering.The wear rates of CoCrMo alloy without Ti-DLC coating and W-DLC coating were measured by friction and wear experiments. The wear rates of CoCrMo alloy were 15.25 脳 10 ~ 10 ~ (-6) and 0.19 脳 10~(-6)mm~3 ~ (-1) respectively.The results show that the wear resistance of the substrate is obviously improved after the coating, and the wear resistance of the W-DLC plated sample is better than that of the Ti-DLC plated sample.Raman analysis showed that the coating exhibited excellent wear resistance due to partial graphitization.
【作者單位】： 廣州有色金屬研究院;中南大學(xué);
【基金】：National Science and Technology Support Program of China(2012BAI18B04) International Cooperation Projects in Guangdong Province(2011B050400007)
【分類號】：TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 鄭華均,黃建國;磁控濺射法制備碳化鎢薄膜的研究及應(yīng)用進(jìn)展[J];浙江化工;2005年01期

2 楊加志;趙成剛;劉曉麗;于俊偉;孫東平;唐衛(wèi)華;;采用磁控濺射法在細(xì)菌纖維素膜上制備高性能的銦錫氧化物薄膜(英文)[J];Chinese Journal of Chemical Engineering;2011年02期

3 馬偉偉;李剛;周小康;梁玉強(qiáng);劉會友;;磁控濺射法制備阻隔包裝紙的研究[J];中華紙業(yè);2011年20期

4 張茂國,陳華;磁控濺射法制備硅鉬薄膜及其性能表征[J];稀有金屬材料與工程;2005年07期

5 許小亮;王燁;趙亞麗;牟威圩;施朝淑;;磁控濺射法制備的納米金薄膜的工藝條件和結(jié)構(gòu)分析[J];功能材料;2006年08期

6 宋秀峰;韓艷春;何洪;沈源;;磁控濺射法制備AlN薄膜的研究進(jìn)展[J];山東陶瓷;2006年06期

7 王東,齊宏進(jìn);磁控濺射法制備防水透濕織物的性能研究[J];棉紡織技術(shù);2002年01期

8 程曉農(nóng);宋娟;嚴(yán)學(xué)華;;磁控濺射法制備ZrW_2O_8/Cu梯度薄膜[J];硅酸鹽學(xué)報(bào);2007年11期

9 趙印中;許e，

本文編號：1743323