【摘要】：利用原子力顯微鏡、顯微硬度儀和摩擦磨損儀等測試方法研究表面機械沖擊形變和穩(wěn)定化熱處理誘發(fā)Cu30Ni合金的顯微組織結(jié)構(gòu)變化和摩擦磨損性能。結(jié)果表明:與原始試樣相比,機械沖擊形變誘發(fā)非穩(wěn)定晶界組織結(jié)構(gòu)形成,穩(wěn)定化熱處理促進細化組織結(jié)構(gòu)的非穩(wěn)定晶界向穩(wěn)定或亞穩(wěn)定晶界轉(zhuǎn)變,導致顯微硬度從93HV提高到297HV,磨損速率從4.2mm3/m降低到0.41mm3/m,摩擦因數(shù)μ從0.35降低到0.32,且在機械沖擊形變和穩(wěn)定化熱處理的試樣磨痕形貌中未觀察到顯微裂紋存在。
[Abstract]:The microstructure and tribological properties of Cu30Ni alloy induced by mechanical impact deformation and stabilization heat treatment were studied by means of atomic force microscope, microhardness tester and friction and wear tester.The results show that mechanical shock deformation induces the formation of unsteady grain boundary structure, and the stable heat treatment promotes the transformation from the unsteady grain boundary to the metastable grain boundary.The microhardness increased from 93HV to 297HV, the wear rate decreased from 4.2mm3/m to 0.41mm3 / m, the friction coefficient 渭 decreased from 0.35 to 0.32.The microcracks were not observed in the wear trace morphology of the specimens subjected to mechanical shock deformation and stabilized heat treatment.
【作者單位】： 江蘇省先進結(jié)構(gòu)材料與應用技術(shù)重點實驗室;南京工程學院材料工程學院;撫順特殊鋼股份有限公司質(zhì)量處;
【基金】：國家自然科學基金-青年科學基金項目(51301086) 江蘇省基礎(chǔ)研究計劃(自然科學基金)-青年基金項目(BK20130738)
【分類號】：TG146.11

【相似文獻】

相關(guān)期刊論文 前4條

1 Graham Budden;;防護與舒適并存的新型抗機械沖擊防護服[J];紡織導報;2006年09期

2 程衛(wèi)東;李琳;劉亞;;蟠桃汁飲料產(chǎn)業(yè)化生產(chǎn)中質(zhì)量影響因素的探討[J];食品科技;2007年02期

3 李翔;李雙躍;任朝富;羅澤元;張亞南;田坪;;CXM80高速超細機械沖擊磨的開發(fā)與研制[J];礦業(yè)研究與開發(fā);2010年01期

4 ;[J];;年期

，

本文編號：1730219