本文選題：射頻磁控濺射　切入點(diǎn)：NiCr薄膜　出處：《材料導(dǎo)報(bào)》2015年S2期

【摘要】：采用射頻磁控濺射技術(shù)在不銹鋼基底上制備NiCr金屬薄膜,研究不同的氬氣壓強(qiáng)對(duì)樣品形貌和光學(xué)、附著力性能的影響。結(jié)果表明:所制備的NiCr薄膜在中遠(yuǎn)紅外區(qū)都具有較高的反射率,平均值約為0.92,附著力級(jí)別均能達(dá)到5B;氬氣壓強(qiáng)對(duì)薄膜的性能具有較大的影響,具體表現(xiàn)為:隨著壓強(qiáng)的增大,薄膜的結(jié)晶度先上升后下降,均勻性先變好后變壞,在壓強(qiáng)為4Pa時(shí)薄膜質(zhì)量最好。
[Abstract]:NiCr thin films were fabricated on stainless steel substrates by radio frequency magnetron sputtering . The effects of different argon pressures on the morphology and optical properties of the films were investigated . The results show that the prepared NiCr films have higher reflectivity in the middle and far infrared regions , the average value is about 0.92 , the adhesion level can reach 5B ; the pressure of argon increases first and then decreases after the increase of the pressure . The uniformity of the films becomes worse . The film quality is best when the pressure is 4 Pa .

【作者單位】： 暨南大學(xué)信息科學(xué)技術(shù)學(xué)院;
【基金】：廣東省教育部產(chǎn)學(xué)研結(jié)合項(xiàng)目(2012B091000111) 廣東省科技計(jì)劃項(xiàng)目(2014A010106014) 中央高�；究蒲袠I(yè)務(wù)費(fèi)專項(xiàng)基金(21612412) 暨南大學(xué)挑戰(zhàn)杯項(xiàng)目(141213045)
【分類號(hào)】：TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 Shan-Tung TU;;Creep behavior of plasma sprayed NiCr and NiCrAl coating-based systems[J];Acta Metallurgica Sinica(English Letters);2011年03期

2 ;Microstructure and Tribological Performances of 25NiCr-Cr_3C_2 Coatings Prepared by Laser-Hybrid Plasma Spraying Technology[J];稀有金屬材料與工程;2011年S4期

3 張東方,潘牧,羅志平;Ni/Al,NiCr粘結(jié)層的耐蝕性能研究[J];山東陶瓷;2003年01期

4 李振鐸,于月光,曾克里,任先京,周恒,林鋒,賈賢賞;Cr_3C_2-25%NiCr料漿中分散劑含量對(duì)其噴霧干燥粉末性能的影響[J];礦冶;2005年03期

5 于華;林耀華;陳春梅;聶書才;彭榮剛;楊豫川;楊?yuàn)檴?;35CrMo鋼表面電火花沉積NiCr合金強(qiáng)化層特性的研究[J];表面技術(shù);2010年04期

6 金云學(xué);岳佳，

本文編號(hào)：1725135