本文選題：氣瓶鋼　切入點(diǎn)：MnV　出處：《鋼鐵釩鈦》2015年06期

【摘要】：研究了34Mn2V鋼經(jīng)不同溫度正火后的力學(xué)性能,分析了不同溫度正火后材料的組織變化對(duì)沖擊韌性的影響。實(shí)驗(yàn)室及工業(yè)試驗(yàn)結(jié)果表明,利用適宜的亞溫正火可顯著提高34Mn2V鋼的沖擊韌性,實(shí)際生產(chǎn)中適當(dāng)降低正火溫度可使34Mn2V鋼具有良好的強(qiáng)韌性,滿足高壓氣瓶技術(shù)條件的要求。
[Abstract]:The mechanical properties of 34Mn2V steel after normalizing at different temperatures were studied. The effect of microstructure changes on impact toughness of 34Mn2V steel after normalizing at different temperatures was analyzed. The impact toughness of 34Mn2V steel can be significantly improved by proper subtemperature normalizing, and the proper lowering of normalizing temperature in practical production can make 34Mn2V steel have good strength and toughness, and meet the requirements of the technical conditions of high pressure gas cylinders.
【作者單位】： 攀鋼集團(tuán)研究院有限公司;
【分類號(hào)】：TG161;TG142.1

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 鐘云龍,劉國(guó)權(quán),劉勝新,張艷,黃建凱,王成,施琪;新型油井管鋼33Mn2V的動(dòng)態(tài)再結(jié)晶規(guī)律研究[J];鋼鐵;2003年02期

2 陸璐;王照旭;王輔忠;;33Mn2V鋼流變應(yīng)力計(jì)算模型研究[J];渤海大學(xué)學(xué)報(bào)(自然科學(xué)版);2012年01期

3 聶輝文;聶俊紅;曾松盛;;鋸片基體用50Mn2V鋼淬透性不良原因分析[J];機(jī)械工程材料;2011年05期

4 胡德山;34Mn2V無(wú)縫氣瓶鋼的冶煉[J];包鋼科技;1996年04期

5 張慧春;王輔忠;劉國(guó)權(quán);陸璐;朱光亞;;新型油井管鋼33Mn2V穿管過(guò)程動(dòng)態(tài)再結(jié)晶晶粒變化的二維數(shù)值模擬[J];兵器材料科學(xué)與工程;2009年05期

6 邢獻(xiàn)軍,由宏新,金巨年;34Mn2V氣瓶用鋼亞溫二次正火低溫改性機(jī)理研究[J];壓力容器;1993年02期

7 陳興元;40Mn2V鋼沖擊韌性惡化的原因[J];機(jī)械工程材料;1992年01期

8 由宏新,邢獻(xiàn)軍,金巨年;亞溫正火提高34Mn2V鋼低溫韌性[J];金屬熱處理;2000年12期

9 秦海青;周桂琴;王進(jìn)保;蒙光海;李運(yùn)海;程柳;;50Mn2V金剛石鋸片激光焊接過(guò)渡層粉末的研制(上)[J];超硬材料工程;2010年03期

10 邢獻(xiàn)軍,金巨年;34Mn2V鋼在正火條件下釩碳化物的析出機(jī)理及其對(duì)力學(xué)性能的影響[J];理化檢驗(yàn)(物理分冊(cè));1996年06期

，

本文編號(hào)：1669965