本文選題：L不銹鋼　切入點：堿性溶液　出處：《表面技術》2015年03期 　論文類型：期刊論文

【摘要】：目的研究316L不銹鋼在堿性硫化物溶液中的應力腐蝕行為,為其在堿性環(huán)境中的適用性提供參考依據。方法采用動電位極化曲線、電化學阻抗(EIS)測量技術、慢應變速率拉伸試驗(SSRT)、U形彎試樣浸泡試驗以及SEM腐蝕形貌分析方法。結果 316L不銹鋼試樣在堿性硫化物溶液中具有較低的應力腐蝕(SCC)敏感性,腐蝕機理主要為陽極溶解型,且SCC敏感性隨著p H升高而降低。結論316L不銹鋼試樣在堿性Na Cl/Na2S溶液中雖然表現出應力腐蝕特征,但敏感性較低,適用于該實驗模擬的堿性溶液中。
[Abstract]:Aim to study the stress corrosion behavior of 316L stainless steel in alkaline sulfide solution and to provide a reference for its applicability in alkaline environment. Slow strain rate tensile test (SSRTX) and SEM corrosion morphology analysis method were used. Results 316L stainless steel has lower stress corrosion (SCC) sensitivity in alkaline sulfide solution, and the corrosion mechanism is mainly anodic dissolution. The sensitivity of SCC decreases with the increase of pH. Conclusion although 316L stainless steel samples exhibit the characteristics of stress corrosion in alkaline Na Cl/Na2S solution, the sensitivity is relatively low, which is suitable for the alkaline solution simulated by this experiment.
【作者單位】： 北京科技大學腐蝕與防護中心;教育部腐蝕與防護重點實驗室;
【基金】：國家高技術研究發(fā)展計劃(863計劃,2012AA040105) 國家自然科學基金(51471034) 北京市青年英才計劃資助~~
【分類號】：TG172.9

【參考文獻】

相關期刊論文 前6條

1 董超芳;關w扌，

本文編號：1610180