本文選題：耐磨鋼　切入點(diǎn)：鈮　出處：《工程科學(xué)學(xué)報(bào)》2015年07期 　論文類型：期刊論文

【摘要】：通過光學(xué)顯微鏡、掃描電鏡、透射電鏡、力學(xué)性能測試等手段分析了微量合金元素鈮對低合金耐磨鋼組織和性能的影響.加入質(zhì)量分?jǐn)?shù)為0.034%的Nb后,耐磨鋼的硬度提高HB 9,-20℃夏比沖擊功從29.4 J提高到37.6 J,耐磨性能提高3.5%.硬度和韌性提高的主要原因是組織的細(xì)化和析出強(qiáng)化,含Nb鋼在奧氏體化過程中析出納米級的細(xì)小Nb C第二相,并且釘扎奧氏體晶界,抑制晶粒的長大,釘扎類型符合Zener模型,但不同于之前研究者所得的比例系數(shù).
[Abstract]:The effect of niobium on the microstructure and properties of low alloy wear resistant steel was analyzed by means of optical microscope, scanning electron microscope, transmission electron microscope and mechanical property test. The hardness of wear-resistant steel was increased from 29.4 J to 37.6 J in summer, and the wear resistance was increased by 3.5J. The main reasons for the increase of hardness and toughness were the refinement of microstructure and precipitation and strengthening. In the austenitizing process of NB containing steel, the fine NB C second phase is precipitated, and the grain boundary of austenite is pinned to restrain the grain growth. The type of pinning conforms to the Zener model, but it is different from the proportional coefficient obtained by previous researchers.
【作者單位】： 北京科技大學(xué)冶金工程研究院;現(xiàn)代交通金屬材料與加工技術(shù)北京實(shí)驗(yàn)室;
【基金】：國家高技術(shù)研究發(fā)展計(jì)劃資助項(xiàng)目(2012AA03A508)
【分類號】：TG142.72

【參考文獻(xiàn)】

相關(guān)期刊論文 前8條

1 趙素;張立;徐國棟;李金富;;Nb-Ti微合金鋼中第二相析出的熱力學(xué)計(jì)算[J];寶鋼技術(shù);2012年02期

2 ;Effect of Microstructure Refinement on the Strength and Toughness of Low Alloy Martensitic Steel[J];Journal of Materials Science & Technology;2007年05期

3 Y.Prawoto;N.Jasmawati;K.Sumeru;;Effect of Prior Austenite Grain Size on the Morphology and Mechanical Properties of Martensite in Medium Carbon Steel[J];Journal of Materials Science & Technology;2012年05期

4 付俊巖;Nb微合金化和含鈮鋼的發(fā)展及技術(shù)進(jìn)步[J];鋼鐵;2005年08期

5 曹建春;雍岐龍;劉清友;孫新軍;;含鈮鉬鋼中微合金碳氮化物沉淀析出及其強(qiáng)化機(jī)制[J];材料熱處理學(xué)報(bào);2006年05期

6 趙英利;時(shí)捷;曹文全;惠衛(wèi)軍;謝剛;;加熱溫度對含Nb中碳鋼奧氏體晶粒長大的影響[J];材料熱處理學(xué)報(bào);2010年04期

7 趙冬偉;曹建春;周曉龍;米永峰;雍岐龍;鄧?yán)?;變形Nb-Mo鋼中碳氮化物在奧氏體中的析出[J];材料熱處理學(xué)報(bào);2012年05期

8 ;Effect of Niobium and Titanium on Dynamic Recrystallization Behavior of Low Carbon Steels[J];Journal of Iron and Steel Research(International);2008年03期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 陳蓉;時(shí)捷;董瀚;劉燕林;顧玉麗;榮凡;;含氮奧氏體鋼與馬氏體鋼的抗彈行為研究[J];兵器材料科學(xué)與工程;2006年02期

2 袁向前;薛鵬;孔偉;焦四海;;鈮微合金化鋼組織—性能關(guān)系模型的研究[J];寶鋼技術(shù);2012年02期

3 李龍飛;陽鋒;楊王s，

本文編號：1584695