文獻名稱：鑄造鋁合金精煉技術現(xiàn)狀及發(fā)展

    前言：闡述了鑄造鋁合金的氣孔形成機制、精煉理論及各種精煉技術的特點、研究現(xiàn)狀和發(fā)展前景。旋轉噴頭吹氣技術、FILD法、MINT法、FIP法和Heproject法等新型復合精煉技術的出現(xiàn),極大地提高了鋁合金熔體精煉水平。
    The gas porosity formation mechanism and refining theory of aluminum casting alloys are systematically summarized and the features, research progresses and prospects of the refining technologies are comprehensively presented. The newly-developed multiple refining technologies, including rotary spray refining processes, FILD, MINT, FIP and Heproject mobile rotary flux feeder, etc, have greatly improved the purity level of molten aluminum.

文獻名稱 鑄造鋁合金精煉技術現(xiàn)狀及發(fā)展

Article Name
英文(英語)翻譯 Progress and Prospect of Refining Technologies of Aluminum Casting Alloys;

作者 馮鵬發(fā); 唐靖林;

Author FENG Peng-fa;TANG Jing-lin（Department of Mechanical Engineering;Tsinghua University;Beijing 100084;China）;

作者單位
Author Agencies 清華大學機械工程系; 清華大學機械工程系 北京100084;

文獻出處
Article From 中國科學院上海冶金研究所; 材料物理與化學(專業(yè)) 博士論文 2000年度

關鍵詞 鑄造鋁合金; 氣孔; 精煉動力學; 復合精煉技術;

Keywords aluminum casting alloys;gas porosity;refining dynamics;multiple refining technologies;

淬火介質對AS7G03鑄造鋁合金性能的影響
固溶溫度對ZL210A鑄造鋁合金砂型試樣力學性能和微觀組織的影響
擠壓鑄造鋁合金彈粘塑性本構模型
鑄造方法對ZL210A鑄造鋁合金力學性能和斷口形貌的影響
A356鑄造鋁合金的疲勞裂紋萌生及短裂紋擴展研究
銀對Al-Cu-Mg-Mn鑄造鋁合金性能的影響
擠壓鑄造鋁合金高溫力學行為試驗
高壓開關殼體用高強鑄造鋁合金的研究
5T有芯感應熔鋁電爐熔煉鑄造鋁合金的實踐
鑄造鋁合金圓錠溫度場實驗研究和數(shù)值模擬

  本文關鍵詞：鑄造鋁合金精煉技術現(xiàn)狀及發(fā)展，由筆耕文化傳播整理發(fā)布。