文獻(xiàn)名稱：Al-Si系鑄造高強(qiáng)度鋁合金的制備技術(shù)研究

    前言：輕量化是我國高速列車發(fā)展的關(guān)鍵技術(shù)之一。我國很多鐵路牛輛的關(guān)鍵零部件，山于結(jié)構(gòu)尺寸大且形狀復(fù)雜，目前仍然采用傳統(tǒng)的鋼鐵，選擇合適的熔體澆注溫度，配合真空攪拌除氣措施，使鑄件在真空下充型，壓力下凝固，減少氣體，提高致密度，孔隙率最低可達(dá)0.03％，由此可使A356...
    Weight reduction is one of the key techniques for the development of high-speed train in China. Presently in our country, however, most of the key components of the high-speed train are made of iron and steel due to their large dimension and complex shape, which makes the train have high weight and limits the technical advancement of high-speed train. Therefore, it is of theoretical and practical significance to explore a kind of new lighter material with high strength to substitute the present iron a...

文獻(xiàn)名稱 Al-Si系鑄造高強(qiáng)度鋁合金的制備技術(shù)研究

Article Name
英文(英語)翻譯 Research on Preparation Technique for High Strength Casting Aluminum Alloy of Al-Si Series;

作者 詹遠(yuǎn)光; 導(dǎo)師:韓建民;

Author

作者單位
Author Agencies 北京交通大學(xué);

文獻(xiàn)出處
Article From 中國科學(xué)院上海冶金研究所; 材料物理與化學(xué)(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 A356; 真空調(diào)壓成型; 孔隙率; T6熱處理; 輕量化材料;

Keywords A356;vacuum adjustable pressure casting;porosity;T6 heat treatment;lightweight material;

A356鑄造鋁合金的疲勞裂紋萌生及短裂紋擴(kuò)展研究
A356合金流動性測試研究
固液相區(qū)等溫保溫時(shí)A356鋁合金半固態(tài)初生相形貌演變特征
A356合金熔體中Al_2O_3夾雜對變質(zhì)劑Sr的影響
A356鋁合金半固態(tài)觸變壓鑄成型技術(shù)研究與展望
Al-Ti-C-Sr對A356合金組織和性能的影響
半固態(tài)A356鋁合金流變擠壓鑄造工藝
Sr對(Al_2O_3+Al_3Zr)_p/A356復(fù)合材料組織及性能的影響
A356合金流變壓鑄成型試驗(yàn)研究
Si、Mg對鋁輪轂用A356合金流動性的影響

  本文關(guān)鍵詞：Al-Si系鑄造高強(qiáng)度鋁合金的制備技術(shù)研究，，由筆耕文化傳播整理發(fā)布。