【摘要】：超高周疲勞的研究可以滿足某些特殊零部件極高循環(huán)周次的要求。綜述了近年來(lái)超高周疲勞的研究進(jìn)展,從S-N曲線的特征、斷面上的魚眼形貌以及裂紋的萌生與擴(kuò)展特征等方面介紹了超高周疲勞的典型特征。分析了影響超高周疲勞的若干因素,如氫的作用、加載頻率、應(yīng)力比和晶粒尺寸等。進(jìn)而提出了一些今后超高周疲勞的研究方向:超高周疲勞裂紋擴(kuò)展的微觀機(jī)理、擴(kuò)展速率尤其是微觀、宏觀上的控制參量的研究以及確定魚眼與ODA區(qū)邊緣的應(yīng)力強(qiáng)度因子范圍對(duì)內(nèi)部裂紋擴(kuò)展門檻值的影響作用。
[Abstract]:The research on super-high cycle fatigue can meet the requirements of very high cycle cycles for some special parts. The research progress of ultra-high cycle fatigue in recent years is reviewed. The typical characteristics of super-high cycle fatigue are introduced from the characteristics of S-N curve, the shape of fish eye on the cross-section and the characteristics of crack initiation and propagation. Some factors affecting ultra-high cycle fatigue, such as the effect of hydrogen, loading frequency, stress ratio and grain size, are analyzed. Furthermore, some research directions of ultra-high cycle fatigue in the future are put forward: the micro-mechanism of crack growth, especially the growth rate of super-high-cycle fatigue crack, especially the micro-cycle fatigue crack growth rate. The macro-control parameters and the influence of the stress intensity factor range on the internal crack growth threshold of the fish eye and the edge of the ODA region were determined.
【作者單位】： 河北工業(yè)大學(xué)材料科學(xué)與工程學(xué)院;裝甲兵工程學(xué)院裝備再制造技術(shù)國(guó)防科技重點(diǎn)實(shí)驗(yàn)室;
【基金】：國(guó)家自然科學(xué)基金重點(diǎn)項(xiàng)目(51535011) 國(guó)防973計(jì)劃(61328304)
【分類號(hào)】：TG113.255

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 周為富;趙振華;陳偉;;鈦合金高周疲勞特性的影響因素分析[J];現(xiàn)代機(jī)械;2009年03期

2 朱曉陽(yáng);奚建法;;低碳鋼在高周疲勞循環(huán)下的循環(huán)硬化問(wèn)題研究[J];機(jī)械強(qiáng)度;1991年02期

3 蔡俊鴻;;探討延長(zhǎng)高周疲勞零件壽命的某些途徑[J];四川冶金;1993年03期

4 關(guān)昕;孟延軍;;超高周疲勞的研究進(jìn)展[J];鋼鐵研究;2009年01期

5 張海威;何宇廷;程禮;高潮;張騰;;鈦合金超高周疲勞性能試驗(yàn)研究[J];航空材料學(xué)報(bào);2013年03期

6 鄧瑛;韓秀全;邵杰;鄧武警;;鈦合金三層空心結(jié)構(gòu)模擬件設(shè)計(jì)及高周疲勞實(shí)驗(yàn)[J];航空制造技術(shù);2013年16期

7 王紅衛(wèi)，楊大智，陳，

本文編號(hào)：2462301