【摘要】：對(duì)齒輪鍛坯進(jìn)行了三種不同工藝的正火處理,并進(jìn)行了耐磨損性能和力學(xué)性能的測(cè)試與分析。結(jié)果表明,與常規(guī)正火相比,等溫正火試樣的磨損體積減小35%,抗拉強(qiáng)度、屈服強(qiáng)度和斷后伸長(zhǎng)率分別提高13%、25%、27%;磁場(chǎng)正火試樣的磨損體積減小63%,抗拉強(qiáng)度、屈服強(qiáng)度和斷后伸長(zhǎng)率分別提高28%、38%、46%。汽車齒輪鍛坯正火工藝優(yōu)選磁場(chǎng)正火工藝。
[Abstract]:The normalizing treatment of gear forging billet with three different processes was carried out, and the wear resistance and mechanical properties were tested and analyzed. The results showed that the wear volume of isothermal normalizing sample decreased by 35%, and the tensile strength, yield strength and elongation after break increased by 13%, 25% and 27%, respectively. The wear volume decreased by 63%, tensile strength, yield strength and elongation after break increased by 28%, 38% and 46%, respectively. Optimization of magnetic field normalizing process for automobile gear forging billet.
【作者單位】： 包頭職業(yè)技術(shù)學(xué)院;
【基金】：內(nèi)蒙古自治區(qū)高等學(xué)�？茖W(xué)研究項(xiàng)目(NJZC14386)
【分類號(hào)】：TG156.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 金榮植;;汽車齒輪熱處理車間環(huán)保、安全防火、防爆的設(shè)計(jì)與安裝[J];汽車工藝與材料;2009年07期

2 韓丕偉;;汽車齒輪的硝鹽淬火[J];現(xiàn)代零部件;2011年02期

3 鄭書芳;高永強(qiáng);;前清洗對(duì)汽車齒輪熱處理畸變的影響[J];金屬加工(熱加工);2011年17期

4 雯;;汽車齒輪包裝防銹方法的改進(jìn)[J];材料保護(hù);1965年03期

5 周德華;;20MnMoB鋼制造重型汽車齒輪的試驗(yàn)與應(yīng)用[J];機(jī)械;1986年02期

6 ;輕型汽車齒輪工藝探析[J];機(jī)械科學(xué)與技術(shù);1989年06期

7 方和杰;新型高效多用途淬火油在汽車齒輪淬火中的應(yīng)用[J];金屬熱處理;1996年06期

8 黃麗榮;湯宏智;;汽車齒輪硬化層深的設(shè)計(jì)[J];熱處理技術(shù)與裝備;2008年06期

9 孫朝國(guó);關(guān)于汽車齒輪花鍵孔推孔整形的研究[J];鑄鍛熱;1998年02期

10 曹穎;韓克甲;劉露;;重卡汽車齒輪開裂失效分析[J];熱處理技術(shù)與裝備;2014年03期

相關(guān)會(huì)議論文 前1條

1 劉志儒;閻牧夫;王勇;江建明;唐寧;王冶;王鴻春;賈玉山;吳德斌;金永植;陳云生;;汽車齒輪滲碳存在問(wèn)題與對(duì)策采用稀土共滲技術(shù)[A];2005年（西安）齒輪材料與熱處理工藝技術(shù)發(fā)展研討會(huì)齒輪熱處理論文集[C];2005年

相關(guān)碩士學(xué)位論文 前2條

1 涂小龍;重型汽車齒輪熱處理變形控制[D];浙江大學(xué);2005年

2 趙亮;汽車齒輪滾齒切削過(guò)程研究及其工藝參數(shù)選擇[D];哈爾濱理工大學(xué);2006年

，

本文編號(hào)：2436760