【摘要】：采用涂刷法,將Ni60粉末均勻刷涂到42Cr Mo基體的表面形成預(yù)涂層。利用電接觸表面強(qiáng)化技術(shù)對(duì)預(yù)涂層進(jìn)行強(qiáng)化,獲得強(qiáng)化層。對(duì)該強(qiáng)化層進(jìn)行顯微組織、顯微硬度、相結(jié)構(gòu)和抗熱震性能研究。結(jié)果表明:電接觸強(qiáng)化工藝使涂層孔隙率減少,致密性增加,同時(shí)提高了涂層的硬度和抗熱震性能。
[Abstract]:The Ni60 powder was evenly brushed to the surface of 42Cr Mo substrate to form a pre-coating. The electric contact surface strengthening technique was used to strengthen the pre-coating and the strengthening layer was obtained. The microstructure, microhardness, phase structure and thermal shock resistance of the strengthened layer were studied. The results show that the porosity and densification of the coating are decreased and the hardness and thermal shock resistance of the coating are improved by the electric contact strengthening process.
【作者單位】： 東華大學(xué)機(jī)械學(xué)院紡織裝備教育與研究中心;
【基金】：上海市重點(diǎn)學(xué)科建設(shè)資助項(xiàng)目(B602)
【分類號(hào)】：TG174.4

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 向文才;;對(duì)電接觸爐有關(guān)公式的認(rèn)識(shí)[J];金屬制品;1989年03期

2 楚振斌;電接觸磨削實(shí)驗(yàn)報(bào)告[J];機(jī)床與工具;1957年12期

3 趙志明;電接觸爐電壓公式的探討及對(duì)傳統(tǒng)公式的質(zhì)疑[J];金屬制品;1988年02期

4 趙志明;電接觸爐電壓公式中有關(guān)鋼絲預(yù)熱溫度的探討及計(jì)算[J];金屬制品;1990年01期

5 鐘玉川;;電接觸切割設(shè)備[J];機(jī)械設(shè)計(jì)與制造;1988年01期

6 朱振榮;新型電接觸薄膜保護(hù)劑的發(fā)展[J];宇航材料工藝;1987年05期

7 胡冀遠(yuǎn);蔡建國(guó);;利用電接觸爐生產(chǎn)正火鋼絲[J];金屬制品;1991年05期

8 陳定一;居德明;;電接觸電阻加熱擠(滾)壓高鉻鑄鐵的實(shí)驗(yàn)研究[J];安徽工學(xué)院學(xué)報(bào);1989年01期

9 鐘燦賢;彈簧鋼件在水介質(zhì)中電接觸處理法[J];國(guó)外金屬熱處理;1997年01期

10 陳定一;電接觸電阻加熱擠壓鎳、鉻金合鑄鐵[J];機(jī)床;1987年02期

相關(guān)會(huì)議論文 前1條

1 于軍琪;孫龍杰;席愛民;;鋼絲電接觸運(yùn)動(dòng)加熱溫度的模糊神經(jīng)網(wǎng)絡(luò)控制[A];全國(guó)冶金企業(yè)計(jì)控網(wǎng)絡(luò)化研討會(huì)論文集[C];2003年

相關(guān)碩士學(xué)位論文 前4條

1 朱浩;42CrMo鋼表面涂層制備工藝的研究[D];東華大學(xué);2017年

2 郝曉磊;電接觸強(qiáng)化預(yù)涂層的制備[D];東華大學(xué);2017年

3 羅湘;高性能鎳基厚涂層的制備工藝及強(qiáng)化[D];東華大學(xué);2017年

4 胡禎;YSZ活性擴(kuò)散障層抗熱震性能的研究[D];西安建筑科技大學(xué);2016年

，

本文編號(hào)：2422681