【摘要】：研究了TC4鈦合金薄板經(jīng)普通退火、α+β兩相區(qū)固溶加時效處理及β單相區(qū)固溶加普通退火處理后,顯微組織與力學(xué)性能的關(guān)系。結(jié)果表明,普通退火處理對TC4鈦合金板材顯微組織的影響較小,α+β兩相區(qū)固溶加時效處理后能夠獲得雙態(tài)組織,而β單相區(qū)固溶加普通退火處理能獲得粗大的魏氏組織;其中雙態(tài)組織的TC4鈦合金薄板表現(xiàn)出優(yōu)異的拉伸性能,而魏氏組織的TC4鈦合金薄板具有較低的疲勞裂紋擴(kuò)展速率及較高的裂紋擴(kuò)展阻力。
[Abstract]:The relationship between microstructure and mechanical properties of TC4 titanium alloy sheet after ordinary annealing, 偽 尾 two-phase solid solution plus aging treatment and 尾 single-phase zone solid solution plus ordinary annealing treatment was studied. The results show that the effect of ordinary annealing on the microstructure of TC4 titanium alloy sheet is relatively small, and the double state microstructure can be obtained after 偽 尾 two-phase region solidification and aging treatment, while 尾 single-phase zone solid solution and ordinary annealing treatment can obtain coarse Weiss microstructure. The TC4 titanium alloy sheet with double structure exhibits excellent tensile properties, while the TC4 titanium alloy sheet with Wei's microstructure has lower fatigue crack growth rate and higher crack propagation resistance.
【作者單位】： 沈陽飛機(jī)工業(yè)(集團(tuán))有限公司;
【分類號】：TG166.5

【參考文獻(xiàn)】

相關(guān)期刊論文 前5條

1 黨鵬;高維娜;付文杰;李輝;呂利強(qiáng);;熱處理對TC4薄板組織與性能的影響[J];熱加工工藝;2014年18期

2 甘章華;梁宇;王錦林;劉靜;;熱處理工藝對TC4鈦合金組織及硬度的影響[J];金屬熱處理;2014年09期

3 葉紅川;張雪華;曲恒磊;李輝;李付國;;兩相區(qū)熱處理對TC4-DT合金板材組織與性能的影響[J];金屬熱處理;2011年12期

4 葉紅川;王彥皓;張雪華;曲恒磊;;β相區(qū)熱處理對TC4-DT合金板材組織和性能的影響[J];熱加工工藝;2011年16期

5 周偉;曲恒磊;趙永慶;李輝;馮亮;陳軍;;TC4-DT合金不同熱處理后的組織與性能[J];金屬熱處理;2006年06期

【共引文獻(xiàn)】

相關(guān)期刊論文 前10條

1 李婷;高菲;傅昊洋;李，

本文編號：2306879