【摘要】：以接頭形式2.5 mm+4.0 mm的5083鋁合金為對象,研究采用回填式攪拌摩擦點焊(RFSSW)時下扎深度、旋轉(zhuǎn)速度、焊接時間三個主要工藝參數(shù)對接頭剪切拉力、交叉拉力及其斷裂方式的影響規(guī)律。結(jié)果表明,當下扎深度2.8 mm、旋轉(zhuǎn)速度2 000 r/min、焊接時間7.5 s時,剪切拉力達到最大值14.62 k N,交叉拉力達到最大值5.49 k N。
[Abstract]:Taking 5083 aluminum alloy with the form of 2.5 mm 4.0 mm as the object, the shear tensile force of the joint was studied by using three main technological parameters of backfill friction stir spot welding (RFSSW), such as the depth of the joint, the speed of rotation and the time of welding. The influence of cross tension and its fracture mode. The results show that the maximum shear tension and cross tension are 14.62 KN and 5.49 KN respectively at the current depth of 2.8 mm, rotation speed of 2 000 rmin and welding time of 7. 5 s.
【作者單位】： 長春工程學(xué)院;
【分類號】：TG453.9

【相似文獻】

相關(guān)期刊論文 前10條

1 吳銘方,于治水,王鳳江;Al_2O_3/AgCuTi/Nb接頭強度及改善[J];焊接技術(shù);2000年05期

2 唐勇;何曉聰;鄭俊超;邢保英;許競楠;;對預(yù)成角薄板粘接接頭強度及其應(yīng)力分析[J];航空材料學(xué)報;2013年04期

3 王瑋，戴瑞玲，朱漢興;粘接單搭接頭強度分析的概況[J];機械強度;1995年04期

4 吳銘方,于治水,蔣成禹,祁凱,程曉農(nóng);反應(yīng)層厚度對Al_2O_3/AgCuTi/Ti-6Al-4V接頭強度的影響[J];稀有金屬材料與工程;2000年06期

5 秦艷文;;增強膠帶接頭強度的接頭處理方法[J];起重運輸機械;2008年05期

6 浩宏奇，王永蘭，金志浩，王笑天;氧化鋁陶瓷釬焊工藝與接頭強度的研究[J];硅酸鹽學(xué)報;1995年02期

7 邢保英;何曉聰;嚴柯科;;粘接劑對自沖鉚-粘接復(fù)合接頭強度的影響及數(shù)理統(tǒng)計分析[J];材料導(dǎo)報;2012年08期

8 孫榮祿，李慕勤，張九海，，黃喜東;中間過渡金屬對鈦合金與不銹鋼擴散焊接頭強度的影響[J];焊接學(xué)報;1996年04期

9 王慕珍,牛濟泰,潘龍修,徐再成,可立盛;SiCw/6061A1激光焊規(guī)范參數(shù)對接頭強度的影響[J];航天工藝;1991年06期

10 何曉聰，趙彥，馬正綱;AE波檢測法在粘接接頭強度評價中的應(yīng)用[J];粘接;1996年03期

相關(guān)會議論文 前2條

1 施志凱;武湛君;;溫度荷載對復(fù)合材料連接頭強度的影響分析[A];第十四屆中國科協(xié)年會第11分會場：低成本、高性能復(fù)合材料發(fā)展論壇論文集[C];2012年

2 侯金保;張蕾;魏友輝;;IC10合金TLP擴散焊接頭強度與分析[A];動力與能源用高溫結(jié)構(gòu)材料——第十一屆中國高溫合金年會論文集[C];2007年

相關(guān)碩士學(xué)位論文 前4條

1 周婷婷;YG10/40Cr連接的界面形貌及接頭性能研究[D];長安大學(xué);2015年

2 劉曉靜;5083鋁合金膠接工藝及接頭性能研究[D];大連交通大學(xué);2013年

3 楊麗群;鋁合金/不銹鋼TIG熔釬焊接頭性能分析[D];大連理工大學(xué);2011年

4 高陽;自然時效與預(yù)應(yīng)變對SAE1004鋼-AA6111鋁合金板材無釘鉚接接頭強度的影響[D];鄭州大學(xué);2014年

本文編號：2288070