【摘要】：采用失重法和掃描電鏡法研究了AZ61與AZ91鎂合金在不同濃度Na Cl溶液中的腐蝕特性,Na Cl溶液的濃度分別為0.001,0.01,0.1,0.2和0.3mol/L。實(shí)驗(yàn)結(jié)果表明,在Na Cl溶液的浸泡實(shí)驗(yàn)中,在相同的浸泡時(shí)間(5d)下,Na Cl溶液濃度增大,AZ61和AZ91鎂合金的腐蝕速率增大,腐蝕程度增強(qiáng),抗腐蝕性減弱。在相同濃度的Na Cl溶液中浸泡相同時(shí)間(5d)的情況下,AZ61鎂合金的抗腐蝕性較好,AZ91鎂合金較差。
[Abstract]:The corrosion characteristics of AZ61 and AZ91 magnesium alloys in Na Cl solution with different concentration were studied by weight loss method and scanning electron microscope. The concentration of, Na Cl solution was 0.001g / L and 0.3mol / L, respectively. The experimental results show that the corrosion rate of AZ61 and AZ91 magnesium alloys increases, the corrosion degree increases and the corrosion resistance weakens when the concentration of, Na Cl solution increases under the same immersion time (5 days) in Na Cl solution. The corrosion resistance of AZ61 magnesium alloy was better than that of AZ91 magnesium alloy when immersed in the same concentration of Na Cl solution for the same time (5 d).
【作者單位】： 呂梁學(xué)院化學(xué)化工系;
【基金】：呂梁學(xué)院校內(nèi)青年基金,AZ系列鎂合金在不同環(huán)境下的腐蝕機(jī)理研究(ZRQN201502);呂梁學(xué)院校內(nèi)青年基金,時(shí)效處理制度對(duì)經(jīng)濟(jì)型雙相不銹鋼2012腐蝕性能的影響研究(ZRQN201501)
【分類號(hào)】：TG146.22

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 張丁非;耿青梅;楊緒盛;余大亮;潘復(fù)生;;新型復(fù)合擠壓工藝中溫度對(duì)AZ61組織和性能的影響[J];材料工程;2014年07期

2 嚴(yán)楷;李元東;馬穎;陳體軍;;熔體處理溫度對(duì)自孕育法制備AZ61半固態(tài)漿料的影響[J];特種鑄造及有色合金;2011年05期

3 陳國(guó)平;周天瑞;閆洪;張發(fā)云;劉宏;;半固態(tài)鎂合金AZ61壓縮變形力學(xué)行為的研究[J];鑄造技術(shù);2007年08期

4 周冰鋒;閆洪;;試驗(yàn)研究半固態(tài)AZ61合金的本構(gòu)關(guān)系[J];中國(guó)機(jī)械工程;2006年17期

5 胡志;閆洪;凌李石保;聶俏;劉少平;;納米SiC顆粒增強(qiáng)AZ61鎂基復(fù)合材料制備工藝的優(yōu)化[J];鑄造;2009年09期

6 彭建;周綢;陶健全;潘復(fù)生;;AZ31與AZ61異種鎂合金的TIG焊研究[J];材料工程;2011年02期

7 ;[J];;年期

相關(guān)會(huì)議論文 前1條

1 周冰鋒;閆洪;;應(yīng)用回歸方法建立半固態(tài)AZ61合金的本構(gòu)關(guān)系[A];第三屆華東六省一市塑性工程學(xué)術(shù)年會(huì)論文集[C];2005年

相關(guān)碩士學(xué)位論文 前1條

1 王晨;鎂合金AZ61熱變形特性及錐齒輪熱鍛成形研究[D];上海交通大學(xué);2012年

，

本文編號(hào)：2276067