本文選題：稀土元素 + Sn-.Cu　； 參考：《鑄造技術(shù)》2017年11期

【摘要】：研究了不同含量的稀土元素Er對(duì)Sn-0.7Cu釬料組織及性能的影響,并利用XRD和SEM對(duì)添加稀土元素前后釬料的微觀組織進(jìn)行了分析。結(jié)果表明,隨著稀土含量的增加,釬料的拉伸強(qiáng)度、鋪展面積先增大后減小,總的蠕變量先減小后增大,說(shuō)明添加適量的稀土元素Er可以改善釬料的拉伸性能、鋪展面積和蠕變性能,Er的最佳添加量為0.1%,當(dāng)含量高于0.1%時(shí),釬料的鋪展面積、拉伸強(qiáng)度和蠕變性能均明顯下降;添加適量的稀土元素,還可以抑制Cu6Sn5的生長(zhǎng),使釬料組織得到細(xì)化。
[Abstract]:The effects of different contents of rare earth element er on the microstructure and properties of Sn-0.7Cu solder were studied. The microstructure of the filler metal before and after the addition of rare earth element was analyzed by XRD and SEM. The results show that with the increase of rare earth content, the tensile strength and spreading area of the filler metal first increase and then decrease, and the total creep amount decrease first and then increase, which indicates that adding appropriate amount of rare earth element er can improve the tensile properties of the filler metal. The optimum addition amount of spreading area and creep property (er) is 0.1. When the content is higher than 0.1, the spreading area, tensile strength and creep property of brazing alloy decrease obviously, and the growth of Cu6Sn5 can be inhibited by adding a proper amount of rare earth elements. The microstructure of solder is refined.
【作者單位】： 南充職業(yè)技術(shù)學(xué)院;
【基金】：四川省教育廳自然科學(xué)基金項(xiàng)目資助(16ZB0465)
【分類號(hào)】：TG425

【相似文獻(xiàn)】

相關(guān)期刊論文 前5條

1 趙中魁,周鐵濤,劉培英,陳昌麒;Al-Zn-Mg-Cu-Li-Er合金時(shí)效組織中Er相的TEM觀察[J];稀有金屬材料與工程;2004年10期

2 王文靜;劉子利;劉希琴;胡金東;王立紅;;含Er鎂合金的研究進(jìn)展[J];上海有色金屬;2013年04期

3 ;REGO-FIX公司為ER刀具夾持系統(tǒng)添加了新產(chǎn)品[J];航空制造技術(shù);2012年21期

4 ;REGO-FIX公司ER刀具夾持系統(tǒng)再添新品[J];工具技術(shù);2012年09期

5 郭連平;陳樂(lè)平;尹健;周全;;Er合金化在鎂合金中的作用研究進(jìn)展[J];鑄造技術(shù);2012年08期

相關(guān)會(huì)議論文 前1條

1 羅素琴;潘復(fù)生;湯愛(ài)濤;;稀土元素Er和Y對(duì)鎂合金固溶強(qiáng)化的影響[A];2011中國(guó)材料研討會(huì)論文摘要集[C];2011年

相關(guān)碩士學(xué)位論文 前1條

1 趙靜;微量元素Er和Zr復(fù)合合金化對(duì)鋅鋁合金組織及性能的影響[D];沈陽(yáng)工業(yè)大學(xué);2012年

，

本文編號(hào)：2021333