本文選題：回火溫度 + 高碳鋼　； 參考：《鋼鐵研究學(xué)報(bào)》2017年06期

【摘要】：研究了回火溫度對(duì)高碳鋼斷裂韌性及其他力學(xué)性能的影響。利用緊湊拉伸試樣測(cè)量其平面應(yīng)變斷裂韌度,掃描電鏡(SEM)觀察回火后的組織演變規(guī)律及斷裂韌度試樣斷口形貌。結(jié)果表明:隨著回火溫度的升高,馬氏體逐漸分解消失,從過(guò)飽和α固溶體中析出的碳化物數(shù)量逐漸增多并發(fā)生聚集長(zhǎng)大,強(qiáng)度和硬度下降,塑性、斷裂韌性和沖擊韌性上升。位錯(cuò)強(qiáng)化和固溶強(qiáng)化作用減弱是試驗(yàn)鋼強(qiáng)度降低、韌性升高的主要原因。
[Abstract]:The effect of tempering temperature on fracture toughness and other mechanical properties of high carbon steel was studied. The plane strain fracture toughness of compact tensile specimens was measured and the microstructure evolution and fracture morphology of tempered specimens were observed by SEM (SEM). The results show that with the increase of tempering temperature, martensite gradually decomposes and disappears, and the amount of carbide precipitated from supersaturated 偽 solid solution increases and accumulates and grows, the strength and hardness decrease, and the plasticity, fracture toughness and impact toughness increase. Dislocation strengthening and solution strengthening are the main reasons for the decrease of test steel strength and the increase of toughness.
【作者單位】： 鋼鐵研究總院特殊鋼研究所;晉西工業(yè)集團(tuán)有限責(zé)任公司;
【基金】：國(guó)家自然科學(xué)基金青年基金資助項(xiàng)目(51301042)
【分類(lèi)號(hào)】：TG142.1;TG161

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 曹士暖;;確定碳素鋼回火溫度的經(jīng)驗(yàn)公式[J];金屬熱處理;1960年03期

2 栗世奇;;一些常用鋼的回火溫度表[J];機(jī)械工人技術(shù)資料;1973年04期

3 宋延沛,祝要民,朱景芝;回火溫度對(duì)高碳中錳鋼性能的影響[J];熱加工工藝;2000年06期

4 賀秀麗;關(guān)小軍;徐洪慶;王連杰;李國(guó)保;;回火溫度對(duì)高強(qiáng)度容器鋼組織結(jié)構(gòu)與性能的影響[J];山東輕工業(yè)學(xué)院學(xué)報(bào)(自然科學(xué)版);2007年03期

5 李繼紅;李巖;張海存;支金花;張敏;;回火溫度對(duì)40CrNiMo7鋼組織與性能的影響[J];金屬熱處理;2011年07期

6 王良;;幾種常用鋼回火溫度的確定[J];機(jī)械工人;1958年04期

7 王良;;幾種常用掽回火溫度的確定[J];機(jī)械工人;1958年05期

8 任恒山;;降低回火溫度提高煤水幨，

本文編號(hào)：1966282