本文選題：異步熱軋 + 同步熱軋��； 參考：《東北大學學報(自然科學版)》2017年07期

【摘要】：分別采用同步熱軋及異速比為1.2的異步熱軋對低合金鋼進行熱軋,研究異步熱軋對低合金鋼顯微組織及力學性能的影響機制.結果表明,與同步熱軋相比,異步熱軋可顯著促進低合金鋼奧氏體/鐵素體相變,提高熱軋鋼板厚度方向的組織均勻性.同步熱軋工藝下,鋼板表層為細晶鐵素體層,厚度1/4或1/2處組織為粗大的貝氏體.異步熱軋工藝下,鋼板板厚方向主要為均勻的鐵素體組織.兩種熱軋條件下,實驗鋼的抗拉強度和延伸率相當,分別為710~718 MPa和20%.采用異步熱軋代替同步熱軋后,實驗鋼的屈服強度由526MPa提高至561 MPa.這主要是由于同步熱軋的鋼板相變強化占主導,而異步熱軋的鋼板細晶強化相對較強.
[Abstract]:The influence mechanism of asynchronous hot rolling on microstructure and mechanical properties of low alloy steel was studied by synchronous hot rolling and asynchronous hot rolling with different speed ratio of 1.2. The results show that asynchronous hot rolling can significantly promote austenite / ferrite transformation in low alloy steel compared with synchronous hot rolling and improve the microstructure uniformity in thickness direction of hot rolled steel. In the process of simultaneous hot rolling, the surface layer of the steel plate is fine grain ferrite layer, and the microstructure at 1 / 4 or 1 / 2 thickness of the steel plate is coarse bainite. In the asynchronous hot rolling process, the thickness direction of steel plate is mainly homogeneous ferrite structure. Under two hot rolling conditions, the tensile strength and elongation of the experimental steel are the same, which are 710 ~ 718 MPa and 20% respectively. After synchronous hot rolling was replaced by asynchronous hot rolling, the yield strength of the experimental steel was increased from 526MPa to 561MPa. This is mainly due to the dominant phase transformation strengthening of synchronous hot rolled steel plate, while the fine grain strengthening of asynchronous hot rolled steel plate is relatively strong.
【作者單位】： 東北大學軋制技術及連軋自動化國家重點實驗室;
【基金】：國家自然科學基金資助項目(51204052)
【分類號】：TG142.33;TG335.11

【相似文獻】

相關期刊論文 前10條

1 ;力學性能二級人員取證復習參考題(之一)解答[J];理化檢驗(物理分冊);1997年12期

2 ;力學性能二級人員取證復習參考題(之三)解答[J];理化檢驗(物理分冊);1998年04期

3 陳金寶;高溫力學性能二級人員取證復習參考題(持久部分之五)解答[J];理化檢驗(物理分冊);2000年02期

4 潘葉金;電弧熔鑄的Nb-18Si-5Mo-5Hf-2C復合材料的力學性能[J];中國鉬業(yè);2003年03期

5 張美忠,李賀軍,李克智;三維編織復合材料的力學性能研究現(xiàn)狀[J];材料工程;2004年02期

6 游宇,周新貴;三維編織復合材料的力學性能[J];纖維復合材料;2004年04期

7 羅文波;唐欣;譚江華;趙榮國;;流變材料長期力學性能加速表征的若干進展[J];材料導報;2007年07期

8 嚴振宇;徐強;朱時珍;劉穎;;Sm_2Zr_2O_7-ZrB_2/SiC復合材料的制備及力學性能研究[J];稀有金屬材料與工程;2011年S1期

9 瞿欣;孫汝n，

本文編號：1869691