【摘要】：為了研究工藝參數(shù)對高強(qiáng)鋼板杯形件單道次拉深旋壓成形質(zhì)量的影響規(guī)律,以旋壓件的壁厚分布、直線度以及圓度均值作為評價指標(biāo),基于有限元分析軟件ABAQUS對DP600高強(qiáng)鋼板單道次拉深旋壓成形過程進(jìn)行數(shù)值模擬研究,并進(jìn)行了試驗驗證。結(jié)果表明:在高強(qiáng)鋼板杯形件單道次拉深旋壓成形過程中,隨著旋輪進(jìn)給比f、旋輪圓角半徑rρ以及旋輪與芯模間相對間隙值δ的增大,其壁厚分布的均勻性逐漸變好,直線度逐漸增加;圓度均值呈先減小后增加的趨勢,并且均存在一最小值;當(dāng)f=0.5 mm·r-1、rρ=10 mm及δ=-5%時,DP600高強(qiáng)鋼板杯形件單道次拉深旋壓成形時的質(zhì)量最優(yōu)。
[Abstract]:In order to study the influence of process parameters on the quality of single pass deep spinning of high strength steel sheet cup, the wall thickness distribution, straightness and roundness of spinning parts are taken as the evaluation indexes. Based on the finite element analysis software ABAQUS, the numerical simulation of single pass deep spinning process of DP600 high strength steel plate is carried out, and the experimental results are verified. The results show that the uniformity of wall thickness distribution becomes better with the increase of feed ratio f, radius r 蟻 and the relative gap value 未 between the rotary wheel and the core die in the process of single-pass deep spinning of the high-strength steel plate cup parts, and the results show that the uniformity of the wall thickness distribution becomes better with the increase of the feed ratio of the rotary wheel, the radius r 蟻 of the rotary wheel and the relative gap between the rotary wheel and the core die. The straightness increases gradually, the mean value of roundness decreases first and then increases, and there is a minimum value, and the quality is the best when f _ (0.5) mm r ~ (-1) r 蟻 _ (10 mm) and 未 ~ (-5) ~ (-5) are used in single-pass deep spinning forming of cup parts of high strength steel sheet.
【作者單位】： 華南理工大學(xué)機(jī)械與汽車工程學(xué)院;寶山鋼鐵股份有限公司研究院;
【基金】：廣東省公益研究與能力建設(shè)專項項目(2016A010102011)
【分類號】：TG306

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 夏琴香,阮鋒;成形工藝參數(shù)對杯形件單道次拉深旋壓力的影響[J];鍛壓技術(shù);2004年01期

2 齊麥順;;鋁合金輪轂拉深旋壓成形模擬和試驗[J];有色金屬;2010年02期

3 羅杜宇;夏琴香;;基于正交試驗的拉深旋壓制杯工藝參數(shù)研究[J];精密成形工程;2010年02期

4 林波;谷建民;周尚榮;劉建軍;蔡偉;方雷;;超半球殼體多道次拉深旋壓工藝研究[J];機(jī)械工程學(xué)報;2011年06期

5 曾超;張賽軍;夏琴香;謝紅希;;旋輪軌跡和工藝參數(shù)對多道次拉深旋壓成形質(zhì)量的影響研究[J];鍛壓技術(shù);2014年01期

6 林波;周尚榮;劉建軍;谷建民;王德輝;蔡偉;;Q235和1060中厚板多道次拉深旋壓工藝研究[J];鍛壓技術(shù);2010年04期

7 ;[J];;年期

相關(guān)碩士學(xué)位論文 前2條

1 馬菽聰;鋁合金拉深旋壓成形規(guī)律的研究[D];燕山大學(xué);2008年

2 李玉強(qiáng);多道次拉深旋壓成形規(guī)律的研究[D];西北工業(yè)大學(xué);2002年

，

本文編號：1845394