本文選題：鋁合金 + 熱變形　； 參考：《Transactions of Nonferrous Metals Society of China》2016年02期

【摘要】：利用應(yīng)力應(yīng)變曲線、熱加工圖,結(jié)合電子透射電子顯微鏡和背散射衍射技術(shù)研究在變形溫度為350~510°C、應(yīng)變速率為0.001~10 s-1時高鈦6061鋁合金的熱變形行為。結(jié)果表明,該合金的熱壓縮變形流變峰值應(yīng)力隨變形溫度的升高和應(yīng)變速率的降低而降低;在實驗參數(shù)范圍內(nèi)平均熱變形激活能為185 k J/mol;建立了流變應(yīng)力模型;該合金熱變形時主要的軟化機(jī)制為動態(tài)回復(fù);根據(jù)材料動態(tài)模型獲得了高鈦6061鋁合金的熱加工圖,最佳的熱加工窗口溫度為400~440°C,應(yīng)變速率為0.001~0.1 s~(-1)。
[Abstract]:The thermal deformation behavior of high titanium 6061 aluminum alloy was studied by means of stress-strain curve, hot working diagram, electron transmission electron microscope and backscatter diffraction technique at the deformation temperature of 350 擄C and strain rate of 0.001 ~ 10 s ~ (-1). The results show that the rheological peak stress of the alloy decreases with the increase of deformation temperature and the decrease of strain rate, the average activation energy of hot deformation is 185 kJ / mol in the range of experimental parameters, and the rheological stress model is established. The main softening mechanism of the alloy during hot deformation is dynamic recovery, according to the material dynamic model, the hot working diagram of high titanium 6061 aluminum alloy is obtained. The optimum temperature of hot working window is 400 ~ 440 擄C, and the strain rate is 0.001 ~ 0. 1 ~ 0. 1? s ~ (-1).
【作者單位】： 燕山大學(xué)先進(jìn)鍛壓成形技術(shù)與科學(xué)教育部重點實驗室;
【分類號】：TG142.21

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 劉晶元,丁培道,潘復(fù)生,周守則;稀土對6063合金熱變形行為的影響[J];熱加工工藝;1997年04期

2 肖弦;周春華;;鋅合金熱變形行為的研究[J];熱加工工藝;2008年15期

3 楊常春;康永林;王立新;秦升;;Cr20Ni32AlTi合金高溫?zé)嶙冃涡袨檠芯縖J];熱加工工藝;2011年22期

4 馬娟;李志峰;符仁鈺;李麟;;Fe-18Mn-0.6C TWIP鋼的熱變形行為[J];上海金屬;2012年01期

5 熊毅;蔡大勇;趙勝利;文九巴;張春玲;;低碳鋼的熱變形行為[J];熱加工工藝;2008年18期

6 郎玉婧;崔華;蔡元華;張濟(jì)山;;應(yīng)變誘導(dǎo)析出對7050合金連續(xù)熱變形組織的影響[J];中國有色金屬學(xué)報;2012年10期

7 王震;洪權(quán);趙永慶;;鈦合金熱變形行為研究[J];鈦工業(yè)進(jìn)展;2010年03期

8 霍連U，

本文編號：1809588