本文選題：硬釬料 + 熱擠壓模具　； 參考：《焊接》2017年08期

【摘要】：從硬釬料的熱擠壓研究及應用現(xiàn)狀談起,分析了影響釬料熱擠壓的裝備功能、模具性能和工藝因素(速度、溫度、變形指數(shù)、模具形狀)。結(jié)合生產(chǎn)實際闡述了常用的擠壓裝備、經(jīng)典擠壓工藝和主要的模具失效形式及其原因,并針對失效形式提出了提高擠壓模具使用壽命、穩(wěn)定產(chǎn)品質(zhì)量、提高生產(chǎn)效率的多項技術(shù)措施;探討了提高釬料熱擠壓質(zhì)量和效率的技術(shù)途徑。調(diào)查研究發(fā)現(xiàn),優(yōu)良的裝備、適宜的工藝和合理的模具設(shè)計是熱擠壓順利進行的根本保證;模具材料、模具制造工藝和使用制度決定著模具使用的穩(wěn)定性。
[Abstract]:Based on the research and application of hard solder hot extrusion, this paper analyzes the equipment function, die properties and technological factors (speed, temperature, deformation index, die shape) which affect the hot extrusion of brazing filler metal. Combined with the production practice, the common extrusion equipment, classical extrusion process, main die failure forms and their causes are expounded. The service life of extrusion die is improved and the product quality is stabilized according to the failure form. Several technical measures to improve the production efficiency are discussed, and the technical ways to improve the quality and efficiency of hot extrusion of solder are discussed. It is found that excellent equipment, suitable technology and reasonable die design are the fundamental guarantee for the smooth progress of hot extrusion, and the stability of die use is determined by die material, die manufacturing technology and application system.
【作者單位】： 哈爾濱工業(yè)大學先進焊接與連接國家重點實驗室;
【基金】：國家國際科技合作計劃項目(2015DFA50470)
【分類號】：TG425.2

【相似文獻】

相關(guān)期刊論文 前5條

1 薛松柏,張國棟,錢乙余;我國硬釬料生產(chǎn)中的質(zhì)量問題及對策(上)[J];焊接;1997年05期

2 張伶,薛松柏;提高我國硬釬料產(chǎn)品質(zhì)量的對策[J];機電產(chǎn)品開發(fā)與創(chuàng)新;2001年03期

3 鄧鍵,張露菁;國外硬釬料擠壓技術(shù)的現(xiàn)狀與分析[J];焊接;2001年01期

4 董仕節(jié),匡一心,史耀武,周文東;低溫鋁基硬釬料基體成分的計算機輔助設(shè)計[J];湖北汽車工業(yè)學院學報;1996年01期

5 張明凡;;釬焊問答[J];焊接技術(shù);1990年01期

，

本文編號：1795199