【摘要】：為了提高SWRH82B盤(pán)條電阻對(duì)焊接頭的性能,對(duì)SWRH82B盤(pán)條進(jìn)行了電阻對(duì)焊和焊后熱處理,分析了不同焊后熱處理溫度下的焊接接頭組織、拉伸斷口形貌和力學(xué)性能。結(jié)果顯示,焊后熱處理溫度對(duì)焊接接頭組織的粗大程度、鐵素體和二次滲碳體的析出程度具有較大的影響。在合適的熱處理溫度下其焊接接頭組織較細(xì)小均勻,鐵素體和二次滲碳體的析出量小,塑性好。
[Abstract]:In order to improve the performance of SWRH82B wire rod resistance butt welding joint, the resistance butt welding and post welding heat treatment of SWRH82B wire rod were carried out. The microstructure, tensile fracture morphology and mechanical properties of the welded joint at different post-weld heat treatment temperature were analyzed.The results show that the temperature of post-weld heat treatment has a great influence on the coarse degree of microstructure and the precipitation degree of ferrite and secondary cementite.At the appropriate heat treatment temperature, the microstructure of the welded joint is fine and uniform, the amount of precipitation of ferrite and secondary cementite is small, and the plasticity is good.
【作者單位】： 九江學(xué)院;
【基金】：九江學(xué)院校級(jí)科研項(xiàng)目(2013ZD07,2014KJYB018) 江西省教育廳科技落地計(jì)劃項(xiàng)目(KJLD14091) 江西省科技計(jì)劃項(xiàng)目(20133BBE50031) 江西省“卓越工程師教育培養(yǎng)計(jì)劃”實(shí)施成果(贛財(cái)教2011[244]號(hào))
【分類(lèi)號(hào)】：TG407

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 袁慶揚(yáng);;高碳鋼絲的電阻對(duì)焊研究[J];金屬制品;1985年01期

2 唐利;;70鋼鋼絲電阻對(duì)焊裂紋產(chǎn)生原因分析及處理[J];焊接技術(shù);2010年08期

3 唐利;;汽車(chē)環(huán)形鋼絲零件電阻對(duì)焊后裂紋產(chǎn)生原因分析及改進(jìn)措施[J];理化檢驗(yàn)(物理分冊(cè));2010年11期

4 楊輝;;高碳鋼盤(pán)條電阻對(duì)焊質(zhì)量的影響因素分析[J];熱加工工藝;2012年17期

5 李，

本文編號(hào)：1750185