發(fā)布時間：2018-03-26 17:04

  本文選題：大塑性變形　切入點：循環(huán)擴擠　出處：《塑性工程學報》2017年01期

【摘要】：多次循環(huán)擴擠成形技術是一種新型的大塑性變形技術,是制備亞微米或納米級塊體材料的有效方法之一。通過7A04鋁合金經(jīng)過一次循環(huán)擴擠平面變形的有限元模擬分析和擠壓成形實驗,并借助于ZEISS Image Alm金相顯微鏡、ZMT5105電子萬能拉伸材料試驗機、維氏硬度測試計等儀器設備,研究了不同變形道次下的循環(huán)擴擠平面變形對7A04鋁合金的力學性能與顯微組織的影響。研究結果表明:二道次擠壓后試樣的抗拉強度、屈服強度、硬度與伸長率均比一道次的高,晶粒細化效果更明顯。
[Abstract]:The forming technology of multiple cycle expansion extrusion is a new type of large plastic deformation technology. It is one of the effective methods to prepare submicron or nanoscale bulk materials. The finite element simulation analysis and extrusion forming experiment of 7A04 aluminum alloy after one cycle extrusion plane deformation are carried out. And with the aid of ZEISS Image Alm metallographic microscope, ZMT5105 electronic universal tensile material testing machine, Vickers hardness tester and other instruments, The effect of cyclic extruding plane deformation on the mechanical properties and microstructure of 7A04 aluminum alloy was studied. The results showed that the tensile strength and yield strength of the second pass extrusion specimen were obtained. Both hardness and elongation are higher than that of the same order, and the effect of grain refinement is more obvious.
【作者單位】： 中北大學機電工程學院;中北大學材料科學與工程學院;
【基金】：山西省自然科學基金資助項目(2013011022-5)
【分類號】：TG146.21;TG306

【相似文獻】

相關期刊論文 前10條

1 林啟權;平面變形擠壓的上限解析解[J];湘潭大學自然科學學報;1996年03期

2 鐘江鴻,李尚健;基于厚向異性的平面變形彎曲過程的有限元分析[J];鍛壓技術;2000年06期

3 王起功;關廷棟;趙振鐸;;平面變形側(cè)向流動過程的上限分析[J];重型機械;1988年07期

4 程鞏固;矩形坯料平面變形滑移線法新解及其應用[J];大型鑄鍛件;1998年01期

5 鐘書明;;T12A鋼無刃切斷刀的微變形淬火[J];金屬熱處理;1986年04期

6 陳志永,張新明,劉楚明,周卓平;面心立方金屬平面變形的屈服應力狀態(tài)分析[J];中南工業(yè)大學學報(自然科學版);2000年04期

7 張培源,嚴波,蔣晗;蜂窩板狀材料反平面變形的等效本構方程[J];重慶大學學報(自然科學版);1995年05期

8 曾德麟;;粉末燒結板坯軋制致密化理論的探討——連續(xù)壓縮平面變形模型[J];中南礦冶學院學報;1985年04期

9 王起功;平面變形問題UBET的研究[J];鍛壓機械;1986年02期

10 趙德文,王國棟,范鶴峰;三角形速度場解析平面變形輥拔與輥擠[J];東北工學院學報;1991年06期

相關會議論文 前1條

1 程鞏固;;矩形坯料平面變形滑移線法新解及其應用[A];中國機械工程學會鍛壓學會第六屆學術年會論文集[C];1995年

，

本文編號：1668761