本文選題：TiAl合金　切入點(diǎn)：β相　出處：《Transactions of Nonferrous Metals Society of China》2017年04期

【摘要】：采用非自耗真空電弧熔煉Ti-45Al-5Nb-xMo-0.3Y(x=0.6,0.8,1.0,1.2)合金試樣,研究Mo含量變化對(duì)含β相TiAl合金顯微組織和力學(xué)性能的影響規(guī)律。研究表明,Mo元素的偏聚使β相呈不連續(xù)網(wǎng)狀分布于γ/α_2片層團(tuán)邊界。當(dāng)Mo含量超過(guò)0.8%時(shí),β相在枝晶間微偏析區(qū)易形成γ相。在T_α轉(zhuǎn)變溫度以上進(jìn)行均勻化熱處理可使β和γ相得到有效消除。對(duì)初始鑄態(tài)和均勻化熱處理態(tài)TiAl合金的組織性能進(jìn)行對(duì)比分析發(fā)現(xiàn),添加過(guò)量的Mo元素容易引起微偏聚,從而降低材料的強(qiáng)度和顯微硬度,而均勻化熱處理可使得其力學(xué)性能得到明顯改善。
[Abstract]:Ti-45Al-5Nb-xMo-0.3YPX 0.6N 0.8N 1.0 1. 2) alloy sample was melted by non-consumable vacuum arc melting. The effect of Mo content on the microstructure and mechanical properties of TiAl alloy containing 尾 phase was studied. The results show that 尾 phase is distributed in discontinuous network at 緯 / 偽 2 lamellar boundary due to segregation of Mo element. When Mo content is more than 0. 8%, 尾 phase is in branch. 緯 phase is easily formed in the intergranular microsegregation region. The 尾 and 緯 phases can be effectively eliminated by homogenizing heat treatment above the T _ 偽 transition temperature. The microstructure and properties of as-cast and homogenized TiAl alloys are compared and analyzed. The addition of excessive Mo elements can easily lead to micro-segregation, thus reducing the strength and microhardness of the materials, and the mechanical properties of the materials can be improved obviously by homogenization heat treatment.
【作者單位】： 哈爾濱工業(yè)大學(xué)材料科學(xué)與工程學(xué)院;哈爾濱工業(yè)大學(xué)金屬精密熱加工國(guó)家級(jí)重點(diǎn)實(shí)驗(yàn)室;
【基金】：Project(51275132)supported by the National Natural Science Foundation of China;Project(2008RFQXG040) supported by the Youth Science and Technology Project of Harbin,China
【分類(lèi)號(hào)】：TG146.23

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 ;DIFFUSION BONDING OF TiAl TO Ti AND TC4 ALLOY[J];Acta Metallurgica Sinica(English Letters);2000年01期

2 ;A STUDY ON ALUMINIDE COATINGS ON TiAl ALLOYS BY PACKCEMENTATION METHOD[J];Acta Metallurgica Sinica(English Edition);2000年06期

3 ;Effects of HIPing Pressure on Microstructures and Properties of TiAl Alloy[J];Journal of Central South University of Technology(English Edition);2000年03期

4 唐建成,黃伯云,劉文勝,賀躍輝;Microstructural evolution of a forged TiAl based alloy during heat treatment at subtransus temperature[J];Transactions of Nonferrous Metals Society of China;2000年02期

5 ;THE STRUCTURE CHANGE OF γ-TiAl IRRADIATED BY 50keV XENON IONS AT ROOM TEMPERATURE[J];Acta Metallurgica Sinica(English Edition);2001年04期

6 吳引江;制造TiAl薄板的新方法[J];鈦工業(yè)進(jìn)展;2001年05期

7 ;Distribution of Nb atom in the TiAl+Nb system[J];Rare Metals;2001年01期

8 ;MEAM Potential with Angular Dependence for TiAl[J];Rare Metals;2001年01期

9 ;Influence of Aluminum Content in γ-TiAl with L1_0 Structure during Ordering Processes[J];Rare Metals;2001年04期

10 馬學(xué)著,沈軍,賈均;Study on Rare Earth-Containing Phases in TiAl Based Alloys Prepared by Non-Equilibrium Solidification Processing[J];Journal of Rare Earths;2001年02期

相關(guān)會(huì)議論文 前10條

1 ;Study on aging phase transformation process in Ni_(42) CrTiAl alloys[A];第二屆全國(guó)掃描電子顯微學(xué)會(huì)議論文集[C];2001年

2 Xiang Zan;Li Ouyang;Yu Wang;Yuehui He;Yong Liu;Weidong Song;;Microstructure Evolution of TiAl under Tensile Impact Loadings[A];中國(guó)材料大會(huì)2012第15分會(huì)場(chǎng)：TiAl合金及先進(jìn)結(jié)構(gòu)金屬間化合物材料論文集[C];2012年

3 Fan Yang;Xiao Li;Nan Tian;Yongfeng Liang;Junpin Lin;;Effect of Nb Addition on the Corrosion Behavior of Porous TiAl Based Alloys in Aqueous Environments[A];中國(guó)材料大會(huì)2012第15分會(huì)場(chǎng)：TiAl合金及先進(jìn)結(jié)構(gòu)金屬間化合物材料論文集[C];2012年

4 Zhiyong Xue;YuanXun Huang;Yongtian Wang;Xiaojing Hai;;Laser Remelting Effect on the Joint Property of Diffusion Bonding of TiAl Intermetallics and TC4 Alloy[A];中國(guó)材料大會(huì)2012第15分會(huì)場(chǎng)：TiAl合金及先進(jìn)結(jié)構(gòu)金屬間化合物材料論文集[C];2012年

5 ;Influence of Heat Treatment on The Precipitation of γ1 Phase in High Nb Containing TiAl-based Intermetallic Alloys[A];2011中國(guó)材料研討會(huì)論文摘要集[C];2011年

6 Chuanyun Wang;Jinshan Li;Bin Tang;Hongchao Kou;;Numerical Analysis of Superplastic Bulging Process of TiAl Sheet[A];中國(guó)材料大會(huì)2012第15分會(huì)場(chǎng)：TiAl合金及先進(jìn)結(jié)構(gòu)金屬間化合物材料論文集[C];2012年

7 付明杰;朱春雷;張繼;;TiAl合金二次變形過(guò)程的數(shù)值模擬與實(shí)驗(yàn)研究[A];第十二屆中國(guó)高溫合金年會(huì)論文集[C];2011年

8 張秉剛;馮吉才;劉會(huì)杰;;TiAl與40Cr鋼直接擴(kuò)散連接的界面組織結(jié)構(gòu)研究[A];第十次全國(guó)焊接會(huì)議論文集（第2冊(cè)）[C];2001年

9 Pengfei Sun;Xiaoou Jin;Yifan Hu;Junpin Lin;;Isothermal Corrosion Behaviors of TiAl-Nb Alloys in Liquid Zn-55Al-1.6Si(wt.%)[A];中國(guó)材料大會(huì)2012第15分會(huì)場(chǎng)：TiAl合金及先進(jìn)結(jié)構(gòu)金屬間化合物材料論文集[C];2012年

10 彭超群;黃伯云;賀躍輝;;TiAl基合金蠕變研究進(jìn)展[A];中國(guó)有色金屬學(xué)會(huì)第三屆學(xué)術(shù)會(huì)議論文集——科學(xué)技術(shù)論文部分[C];1997年

相關(guān)重要報(bào)紙文章 前1條

1 中航工業(yè)黎明航空發(fā)動(dòng)機(jī)（集團(tuán)）有限責(zé)任公司 汪大成;鈦鋁合金(TiAl)應(yīng)用現(xiàn)狀及發(fā)展趨勢(shì)[N];中國(guó)航空?qǐng)?bào);2012年

相關(guān)博士學(xué)位論文 前10條

1 張志勇;高潔凈度TiAl合金及其納米復(fù)合材料的制備，，組織和力學(xué)性能[D];北京科技大學(xué);2015年

2 余龍;高鈮TiAl合金疲勞—蠕變交互作用研究[D];北京科技大學(xué);2016年

3 沈正章;高Nb-TiAl合金板材制備及組織性能研究[D];北京科技大學(xué);2016年

4 舒世立;過(guò)渡族金屬元素和內(nèi)生陶瓷顆粒對(duì)TiAl壓縮性能的影響規(guī)律及機(jī)制[D];吉林大學(xué);2013年

5 楊慧敏;TiAl-5Nb合金定向凝固過(guò)程中組織演化規(guī)律的研究[D];哈爾濱工業(yè)大學(xué);2010年

6 廖翠姣;TiAl合金滲碳處理及其耐蝕性能研究[D];中南大學(xué);2014年

7 羅江山;粉末冶金TiAl基合金的晶粒細(xì)化及其效應(yīng)研究[D];中國(guó)工程物理研究院;2014年

8 彭超群;循環(huán)熱處理對(duì)TiAl基合金組織與性能的影響[D];中南大學(xué);2001年

9 袁勇;TiAl基金屬間化合物的脫溶反應(yīng)和位錯(cuò)結(jié)構(gòu)研究[D];南京大學(xué);2006年

10 高帆;大尺寸TiAl合金鑄錠擠壓開(kāi)坯變形行為與工藝研究[D];東北大學(xué);2011年

相關(guān)碩士學(xué)位論文 前10條

1 邢發(fā)軍;TiAl/TiO_2界面相互作用的第一性原理研究[D];哈爾濱工業(yè)大學(xué);2013年

2 王保棟;TiAl/Al_2O_3界面相互作用第一性原理研究[D];哈爾濱工業(yè)大學(xué);2012年

3 韓波;殘留缺陷對(duì)鑄造TiAl合金擇優(yōu)取向?qū)悠M織疲勞壽命的影響[D];昆明理工大學(xué);2015年

4 李志明;基于Ti-Al-Nb-Cr-B體系的TiAl基合金設(shè)計(jì)與微觀組織研究[D];中國(guó)地質(zhì)大學(xué)(北京);2015年

5 王建成;區(qū)域加熱處理對(duì)TiAl合金組織演化的影響[D];南京理工大學(xué);2015年

6 李明驁;B和C共同添加對(duì)TiAl基合金組織及性能影響研究[D];哈爾濱工業(yè)大學(xué);2015年

7 劉浩;碳含量對(duì)TiAl合金凝固組織及性能的影響[D];哈爾濱工業(yè)大學(xué);2015年

8 代曉爽;TiAl(Si)N涂層的顯微結(jié)構(gòu)及力學(xué)性能研究[D];遼寧科技大學(xué);2015年

9 張震;Ti_(12)Al_(12-x)Mn_x延展性能、抗氧化性能的第一性原理研究[D];東北大學(xué);2014年

10 謝卓成;TiAl合金快速凝固中的微觀結(jié)構(gòu)模擬[D];貴州大學(xué);2015年

本文編號(hào)：1655462