本文選題：離散元　切入點：有限元　出處：《中國有色金屬學報》2017年04期 　論文類型：期刊論文

【摘要】：針對金屬板材固體顆粒介質成形工藝中散體顆粒的離散性能和板材連續(xù)變形特點,提出并構建離散元-有限元耦合仿真模型。通過試驗和數(shù)值模擬相結合的方法,建立鎂合金板材溫熱成形韌性破裂準則,并驗證該準則的有效性。最后結合韌性斷裂準則對AZ31B鎂合金固體顆粒介質筒形件溫熱拉深進行離散元-有限元耦合模擬,對其成形極限進行預測分析,并展開相應條件下的拉深成形試驗。結果表明:基于韌性斷裂準則的離散元-有限元耦合分析方法可以有效預測鎂合金板固體顆粒介質溫熱拉深成形極限。
[Abstract]:According to the discrete properties of granular particles and the characteristics of continuous deformation of sheet metal in solid particle medium forming process, a coupling simulation model of discrete element and finite element is proposed and constructed. The ductile fracture criterion of hot forming of magnesium alloy sheet is established and the validity of the criterion is verified. Finally, the discrete element finite element coupling simulation is carried out to simulate the temperature drawing of AZ31B magnesium alloy solid granular media tube with ductile fracture criterion. The forming limit is predicted and analyzed. The results show that the coupling analysis method of discrete element and finite element based on ductile fracture criterion can effectively predict the forming limit of solid particle medium in magnesium alloy sheet.
【作者單位】： 燕山大學國家冷軋板帶裝備及工藝工程技術研究中心;燕山大學先進鍛壓成形技術與科學教育部重點實驗室(燕山大學);燕山大學車輛與能源學院;
【基金】：國家自然科學基金資助項目(51305385,51305386) 河北省高等學�？茖W技術研究青年基金項目(QN20131080)~~
【分類號】：TG146.22

【相似文獻】

相關期刊論文 前10條

1 張樹艷;馬敘;王志華;楊繼宏;楊全祿;呂麗莎;劉遠鋒;;冷軋深沖板應力成形極限的研究[J];重型機械;2013年02期

2 周亮 ,陳鶴崢;根據(jù)穩(wěn)定理論建立的理論成形極限曲線[J];北京航空學院學報;1986年01期

3 林大為,屠挺生,戴一一,張順才;板料真實成形極限的測定及其應用[J];鍛壓技術;2001年03期

4 李立軍,祝洪川;薄鋼板成形極限曲線的研究[J];物理測試;2003年05期

5 陳R際，

本文編號：1651541