本文選題：雙相不銹鋼　切入點(diǎn)：多層多道焊　出處：《焊接學(xué)報(bào)》2017年05期 　論文類型：期刊論文

【摘要】：采用鎢極氬弧焊制備了雙相鋼焊接接頭,基于熱力學(xué)方法計(jì)算了母材和焊縫的平衡相變過(guò)程,采用OM,SEM,EDS,TEM等方法表征了接頭不同區(qū)域的微觀組織.結(jié)果表明,焊縫中添加鎳顯著促進(jìn)γ形成并抑制Cr_2N析出.焊縫和熱影響區(qū)γ_1主要包含晶粒邊界奧氏體、魏氏奧氏體和晶粒內(nèi)奧氏體,不同類型的奧氏體呈現(xiàn)顯著的成分差異.焊縫和熱影響區(qū)析出兩種類型的γ_2:晶粒內(nèi)γ_2和晶粒間γ_2.γ_2易于在δ內(nèi)和δ/γ_1邊界處富Ni和N元素而貧Cr和Mo元素的區(qū)域析出.Cr_2N主要分布于熱影響區(qū)的δ內(nèi)、δ/γ_2邊界以及δ/δ邊界處.
[Abstract]:The welding joints of dual-phase steel were prepared by TIG welding. The equilibrium phase transition process between base metal and weld was calculated based on thermodynamic method. The microstructure of different regions of the joints was characterized by OMSEMMA-EDSS-TEM. The addition of nickel to the weld significantly promotes 緯 -formation and inhibits Cr_2N precipitation. The weld and HAZ 緯 _ 1 mainly contain grain boundary austenite, Weichlet austenite and intragranular austenite. There are significant differences in composition between different types of austenite. There are two types of 緯 _ 2: 緯 _ 2 in grains and 緯 _ 2 _ 2 in grains. 緯 _ 2 is easy to precipitate in 未 and 未 / 緯 _ 1 boundary where Ni and N are rich and Cr and Mo are poor. Cr2N is mainly distributed in 未, 未 / 緯 -Snap2 boundary and 未 / 未 boundary of heat-affected zone.
【作者單位】： 天津大學(xué)材料科學(xué)與工程學(xué)院;天津市現(xiàn)代連接技術(shù)重點(diǎn)實(shí)驗(yàn)室;
【基金】：國(guó)家自然科學(xué)基金資助項(xiàng)目(51575382)
【分類號(hào)】：TG407

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 黎咸西;熊震宇;;基于視覺傳感的多層多道焊縫圖像特征的識(shí)別[J];南昌航空大學(xué)學(xué)報(bào)(自然科學(xué)版);2011年01期

2 李慧娟;黃振華;張京燾;;厚板多層多道焊的數(shù)值模擬分析[J];宇航材料工藝;2007年05期

3 李慧娟;黃振華;李正任;;多層多道焊焊接工藝數(shù)值模擬技術(shù)[J];焊接技術(shù);2010年11期

4 張華軍;張廣軍;蔡春波;高洪明;吳林;;機(jī)器人多層多道焊縫激光視覺焊道的識(shí)別[J];焊接學(xué)報(bào);2009年04期

5 胥國(guó)祥;杜寶帥;董再勝;朱靜;;厚板多層多道焊溫度場(chǎng)的有限元分析[J];焊接學(xué)報(bào);2013年05期

6 翟紫陽(yáng);王克鴻;;超高強(qiáng)鋼板多層多道焊溫度場(chǎng)有限元分析[J];電焊機(jī);2014年05期

7 危文灝;，

本文編號(hào)：1588646