文獻(xiàn)名稱：離心鑄造高速鋼軋輥鑄造缺陷形成與控制技術(shù)研究

    前言：采用離心鑄造方法制造高速鋼軋輥工藝簡(jiǎn)單,操作方便,但易出現(xiàn)偏析、裂紋、氣孔、縮孔及夾雜等缺陷,影響軋輥的力學(xué)性能和使用性能。采用稀土—鈦復(fù)合變質(zhì)處理改善合金的組織和性能,同時(shí)改進(jìn)離心鑄造工藝參數(shù)可以消除高速鋼軋輥鑄造缺陷,提高力學(xué)性能,改善使用效果。
    Centrifugal casting technology has such characteristics as simple process and easy operation to manufacture high speed steel roll. It is also easy to produce many casting defects such as segregation, crack, air hole, shrinkage and inclusion etc., which decreases the mechanical performances and service properties. Adopting modification process with rare earth (RE) and titanium, the microstructure and performance are obviously improved, and improving centrifugal casting parameter at the same time, the casting...

文獻(xiàn)名稱 離心鑄造高速鋼軋輥鑄造缺陷形成與控制技術(shù)研究

Article Name
英文(英語)翻譯 Study on Defect Formation and Controlling of Centrifugal Casting High Speed Steel Roll;

作者 符寒光; 邢建東;

Author FU Han-guang~1;XING Jian-dong~2 （1. Department of Mechanical Engineering;Tsinghua University;Beijing 100084;2. School of Materials Science & Engineering;Xi'an Jiaotong University;Xi'an 710049;China）;

作者單位
Author Agencies 清華大學(xué)機(jī)械工程系; 西安交通大學(xué)材料科學(xué)與工程學(xué)院 北京; 陜西西安;

文獻(xiàn)出處
Article From 中國(guó)科學(xué)院上海冶金研究所; 材料物理與化學(xué)(專業(yè)) 博士論文 2000年度

關(guān)鍵詞 高速鋼軋輥; 離心鑄造; 鑄造缺陷;

Keywords High-speed steel roll;Centrifugal casting;Casting defect;

高碳高速鋼軋輥中合金元素的作用及成分設(shè)計(jì)
鈦?zhàn)冑|(zhì)高速鋼軋輥的組織和性能
高速鋼軋輥熱處理工藝參數(shù)的預(yù)測(cè)
熱軋粗軋用半高速鋼軋輥材料中碳化物的氧化行為
高速鋼軋輥材料的研究進(jìn)展
珠鋼熱軋機(jī)高速鋼軋輥應(yīng)用技術(shù)開發(fā)
神經(jīng)網(wǎng)絡(luò)的BP算法研究高速鋼軋輥的熱處理工藝
棒線材用小離心高速鋼軋輥鑄造工藝研究
鑄造高速鋼軋輥在熱連軋機(jī)組上的應(yīng)用研究
離心機(jī)雙頭澆注雙金屬復(fù)合鑄管

  本文關(guān)鍵詞：離心鑄造高速鋼軋輥鑄造缺陷形成與控制技術(shù)研究，由筆耕文化傳播整理發(fā)布。