【摘要】：采用金屬鑄造法制備過(guò)共晶Al-22Si合金試樣塊,在光學(xué)顯微鏡上觀察細(xì)化變質(zhì)后過(guò)共晶Al-22Si合金的微觀組織形貌,并測(cè)試其布氏硬度值和銑削表面粗糙度.通過(guò)正交試驗(yàn)探究軸向切深、進(jìn)給量、銑刀轉(zhuǎn)速對(duì)銑削力的影響.實(shí)驗(yàn)結(jié)果表明:細(xì)化變質(zhì)后的過(guò)共晶Al-22Si合金初晶硅尺寸減小,共晶硅呈短棒狀,合金硬度很高,銑削表面粗糙度較小;在銑削加工中,銑刀轉(zhuǎn)速對(duì)合金銑削力的影響最大,其次是軸向切深,最小的是進(jìn)給量.
[Abstract]:The sample blocks of hypereutectic Al-22Si alloy were prepared by metal casting, and the microstructure of the modified hypereutectic Al-22Si alloy was observed by optical microscope. The Brinell hardness and milling surface roughness were tested. The axial tangent depth and feed rate were investigated by orthogonal test. The effect of milling cutter speed on milling force. The experimental results show that the size of primary silicon of the modified hypereutectic Al-22Si alloy is reduced, the eutectic silicon is short rod shape, the hardness of the alloy is very high, and the surface roughness of milling is small. In milling, the milling cutter speed has the greatest influence on the milling force of the alloy, followed by the axial tangent depth and the minimum feed quantity.
【作者單位】： 沈陽(yáng)理工大學(xué)機(jī)械工程學(xué)院;
【分類號(hào)】：TG506
【正文快照】： 過(guò)共晶鋁硅合金具有密度小、比強(qiáng)度高、輕質(zhì)、耐磨等特點(diǎn),主要應(yīng)用于汽車發(fā)動(dòng)機(jī)活塞和車架、飛機(jī)殼體等,在機(jī)械行業(yè)的應(yīng)用日益廣泛[1-2].但是,鋁硅合金在車、銑削加工過(guò)程中有嚴(yán)重的黏刀傾向,常常在前刀面上形成非常堅(jiān)硬的金屬堆積物.這種堆積物被業(yè)界稱為積屑瘤.積屑瘤在切削

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 范婉平,祝光榮;過(guò)共晶鑄鐵定碳定硅樣杯研制成功[J];鑄造;1984年06期

2 王正軍;劉蓮香;;鎂對(duì)過(guò)共晶鋁鐵合金組織形貌的影響[J];中國(guó)有色冶金;2010年05期

3 鄒裕厚;過(guò)共晶鋁硅活塞合金的研制與生產(chǎn)[J];特種鑄造及有色合金;1990年05期

4 吳春京,沈定釗,孔憲候,董振宇;高爐過(guò)共晶鐵水的熱分析定硅[J];北京科技大學(xué)學(xué)報(bào);1990年06期

5 涂贛峰，張成祥，任存治，，李春材，梁西有;鋇對(duì)稀土在過(guò)共晶鐵水中吸收率的影響[J];稀土;1995年06期

6 趙作福;齊錦剛;王建中;;過(guò)共晶鋁-硅合金處理技術(shù)的研究進(jìn)展[J];輕合金加工技術(shù);2010年06期

7 何R

本文編號(hào)：1435933