本文關(guān)鍵詞：U-Cu金屬間化合物制備與表征　出處：《稀有金屬材料與工程》2017年09期 　論文類型：期刊論文

  更多相關(guān)文章： 鈾 金屬間化合物 納米壓痕

【摘要】：研究了U-Cu金屬間化合物的制備與性能。利用納米壓痕、SEM、能譜儀等表征了化合物的形貌、成分和力學(xué)性質(zhì),如彈性模量、硬度等。結(jié)果顯示在一定壓力和溫度作用下,在金屬U和Cu界面獲得了一定厚度的金屬間化合物。擴(kuò)散層成分為Cu和U,Cu/U比例約為78:22。對界面化合物進(jìn)行了微區(qū)納米壓痕測試,結(jié)果顯示U-Cu化合物彈性模量為121 GPa,壓入硬度為5.2 GPa,熱膨脹系數(shù)為7.3×10~(-5)K~(-1)。U-Cu化合物的應(yīng)變硬化效應(yīng)比金屬U明顯。金屬U應(yīng)變率效應(yīng)比U-Cu化合物明顯。
[Abstract]:The preparation and properties of U-Cu intermetallic compounds were studied. The morphology, composition and mechanical properties of the compounds, such as elastic modulus, were characterized by nano-indentation SEM and energy spectrometer. The results show that a certain thickness of intermetallic compound is obtained at the interface of U and Cu under a certain pressure and temperature. The diffusion layer is composed of Cu and U. The Cu/U ratio is about 78: 22.The results show that the modulus of elasticity of U-Cu compounds is 121GPaand the indentation hardness is 5.2 GPa. The strain hardening effect and strain rate effect of metal U are more obvious than that of U, and the strain hardening effect of U is more obvious than that of U Cu.
【作者單位】： 中國工程物理研究院;
【基金】：中物院發(fā)展基金資助(2015B0301046) 國家重大科學(xué)儀器設(shè)備開發(fā)專項(xiàng)“短波長X射線體應(yīng)力無損分析儀開發(fā)及應(yīng)用”(2012YQ130234)資助
【分類號】：TG146.8
【正文快照】： 金屬U作為一種常用的核材料,在核工程許多領(lǐng)硬度、德拜溫度和熱熔,發(fā)現(xiàn)化合物的硬度和彈性模域有廣泛應(yīng)用。通常,U在制備和使用過程中會與其量一般比U金屬高[9]。文獻(xiàn)表明,U能以多個價態(tài)與他金屬在一定溫度下發(fā)生擴(kuò)散行為而生成某些金屬間其他金屬元素化合而存在。而U金屬間化

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 聶大可,李言祥,宋晉生;激光控制反應(yīng)合成金屬間化合物與表面熔覆[J];應(yīng)用激光;2002年02期

2 李愛民,董維芳,孫康寧;金屬間化合物的研究現(xiàn)狀及其最新發(fā)展趨勢[J];現(xiàn)代技術(shù)陶瓷;2004年02期

3 王沿東;孫祖慶;楊王s，

本文編號：1429707