【摘要】：利用壓汞法(MIP)測試了不同鋰渣摻量的C30、C60混凝土的孔結(jié)構(gòu)參數(shù),計(jì)算了被測混凝土的孔體積分形維數(shù)、孔軸線分形維數(shù),并研究了混凝土氣體滲透系數(shù)、鋰渣摻量與孔體積分形維數(shù)、孔軸線分形維數(shù)之間的關(guān)系。結(jié)果表明,混凝土的氣體滲透系數(shù)與孔體積分形維數(shù)相關(guān)性高;C60混凝土在鋰渣摻量為10%時(shí),孔體積分形維數(shù)和孔軸線分形維數(shù)最大;隨著鋰渣摻量的提高,C30混凝土孔體積分形維數(shù)和孔軸線分形維數(shù)呈降低的趨勢。
[Abstract]:The pore structure parameters of C _ (30) C _ (60) concrete with different lithium slag content were measured by (MIP) method. The pore volume fractal dimension and pore axis fractal dimension of concrete were calculated, and the gas permeability coefficient of concrete was studied. The relationship between the content of lithium slag and the fractal dimension of pore volume and pore axis. The results show that the correlation between the gas permeability coefficient and the fractal dimension of pore volume is high. When the content of lithium slag is 10, the fractal dimension of pore volume and the fractal dimension of pore axis are the largest. With the increase of the content of lithium slag, the fractal dimension of pore volume and the fractal dimension of pore axis of C30 concrete decrease.
【作者單位】： 空軍勤務(wù)學(xué)院機(jī)場工程與保障系;
【基金】：國家自然科學(xué)基金項(xiàng)目(51478462,51508565)
【分類號】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前7條

1 王玉鵬;;聚丙烯纖維混凝土抗沖擊性能研究[J];江西建材;2014年12期

2 萬文乾;龍?jiān)?紀(jì)沖;朱燕燕;;鋼纖維混凝土抗沖擊性能的數(shù)值模擬研究[J];南京理工大學(xué)學(xué)報(bào)(自然科學(xué)版);2007年01期

3 王伯昕;黃承逵;;大直徑合成纖維增強(qiáng)混凝土抗沖擊性能的研究[J];建筑材料學(xué)報(bào);2006年05期

4 朱洪波;李晨;閆美珠;吳夢雪;;水泥-聚苯乙烯輕質(zhì)材料的制備及抗沖擊性[J];同濟(jì)大學(xué)學(xué)報(bào)(自然科學(xué)版);2014年05期

5 ;信息與咨詢[J];中國建材;1985年09期

6 李武學(xué);張寶明;;改性聚丙烯纖維對混凝土抗沖擊性能的影響機(jī)理與試驗(yàn)研究[J];天津科技;2011年03期

7 ;[J];;年期

相關(guān)碩士學(xué)位論文 前2條

1 劉臣;合成纖維增強(qiáng)混凝土抗沖擊性能試驗(yàn)研究[D];廣西大學(xué);2012年

2 李佳宇;高硬度高韌性特種玻璃的研究[D];長春理工大學(xué);2014年

，

本文編號：2242578