本文選題：結(jié)晶 + 重結(jié)晶��； 參考：《濕法冶金》2017年01期

【摘要】：研究了高純硝酸鈰的結(jié)晶法制備及重結(jié)晶法純化除雜,采用正交回歸試驗法考察了硝酸鈰結(jié)晶過程中料液初始酸度、結(jié)晶溫度、陳化時間對產(chǎn)品質(zhì)量的影響,以及母液回收利用情況。結(jié)果表明:采用結(jié)晶—重結(jié)晶法可以獲得高純硝酸鈰產(chǎn)品,其中非稀土雜質(zhì)質(zhì)量分數(shù)小于1.5×10-5;確定了潔凈硝酸鈰制備工藝條件。熱分解機制研究結(jié)果表明,硝酸鈰的組成為Ce(NO_3)_3·6H_2O。
[Abstract]:The preparation of high purity cerium nitrate and purification and removal of impurities by recrystallization were studied. The effects of initial acidity, crystallization temperature and aging time on the product quality during the crystallization of cerium nitrate were investigated by orthogonal regression test. And the recovery and utilization of mother liquor. The results show that high purity cerium nitrate can be obtained by crystallization and recrystallization, in which the mass fraction of non-rare earth impurities is less than 1.5 脳 10 ~ (-5), and the preparation conditions of clean cerium nitrate are determined. The results of thermal decomposition show that the composition of cerium nitrate is ce (Nos _ 3) _ 3H _ 2O _ 2.
【作者單位】： 白云鄂博稀土資源研究與綜合利用國家重點實驗室;包頭稀土研究院;瑞科稀土冶金及功能材料國家工程研究中心有限公司;內(nèi)蒙古科技大學化學與化學工程學院;
【分類號】：TQ133.3

【相似文獻】

相關(guān)期刊論文 前7條

1 完顏輝,杭連科,楊汝棟;六偏磷酸鈉與Ce(Ⅲ)及Ce(Ⅳ)的作用[J];稀土;1985年03期

2 田峻,蘇應娟,龔孟濂,雷衡毅,楊燕生;硝酸鈰對大白鼠體內(nèi)乙酰膽堿酯酶活性的影響[J];中山大學學報(自然科學版);1999年02期

3 顏學武,金宗哲,梁金生,王靜,冀志江;硝酸鈰減少OH自由基作用的研究[J];稀有金屬材料與工程;2004年11期

4 孫華;馬洪芳;郭曉斐;馮立明;王s，

本文編號：2117277