本文選題：聚偏氟乙烯乳液 + 改性砂漿　； 參考：《新型建筑材料》2017年08期

【摘要】：聚合物可以顯著改善水泥基材料的工作性、抗彎拉強度及耐腐蝕等性能。研究不同聚灰比(P/C)下,聚偏氟乙烯乳液對水泥砂漿工作性能、力學性能及長期耐久性能的影響。結果表明:聚偏氟乙烯乳液對水泥砂漿具有減水作用,且保水及粘聚性較好,同時具有一定的引氣性;可提高砂漿的變形能力,改善脆性大的缺陷,增加砂漿的拉伸粘結強度;提高砂漿的抗氯離子滲透能力,且吸水率降低、抗收縮性能提高。
[Abstract]:Polymer can significantly improve the workability, flexural tensile strength and corrosion resistance of cement-based materials. The effects of polyvinylidene fluoride (PVDF) emulsion on the working properties, mechanical properties and long-term durability of cement mortar at different P / C ratios were studied. The results show that polyvinylidene fluoride emulsion has water reducing effect on cement mortar, good water retention and cohesion, and good air entrainability, which can improve the deformation ability of mortar, improve the defect of high brittleness and increase the tensile bond strength of mortar. The resistance to chloride ion penetration of mortar is improved, and the water absorption rate is decreased, and the shrinkage resistance is improved.
【作者單位】： 山東華偉銀凱建材科技股份有限公司;
【分類號】：TQ177.62

【相似文獻】

相關期刊論文 前10條

1 鄭鳳;黃征青;;聚偏氟乙烯有機-無機超濾膜性能影響因素的研究進展[J];化學與生物工程;2010年06期

2 劉雙進;王靜榮;劉福諒;;聚偏氟乙烯超濾膜的研究[J];膜科學與技術;1981年02期

3 邵平海，，孫國慶;聚偏氟乙烯微濾膜親水化處理[J];水處理技術;1995年01期

4 吳世清;;化工標準化動態(tài)[J];化工生產與技術;2013年03期

5 姜福昌;;探索以氟聚合物解決化工過程中的難題[J];含氟材料;1980年03期

6 李爭彩;林書玉;;聚偏氟乙烯的性能以及和壓電陶瓷的比較[J];菏澤學院學報;2007年02期

7 王靜榮;聚偏氟乙烯大孔超濾膜的研究[J];環(huán)境科學;1995年01期

8 ;文題錄[J];含氟材料;1981年03期

9 趙玉杰;;聚偏氟乙烯平板膜處理MgCl_2水溶液的實驗研究[J];四川化工;2012年03期

10 曹江;鐘樂;湛含輝;;納米二氧化鈦和羥甲基纖維素對聚偏氟乙烯超濾膜結構和性能的影響[J];湖南工業(yè)大學學報;2009年03期

相關會議論文 前1條

1 王賓;晉衛(wèi);郭偉;呂效平;;聚偏氟乙烯超濾膜超聲輔助清洗及強化膜過濾[A];第三屆全國化學工程與生物化工年會論文摘要集（上）[C];2006年

相關碩士學位論文 前6條

1 周錢華;熱致相分離法制備聚偏氟乙烯中空纖維膜[D];北京工業(yè)大學;2015年

2 沈偉堅;聚偏氟乙烯(PVDF)超濾膜的制備與親水性能的改善[D];浙江理工大學;2016年

3 袁健思;改性聚偏氟乙烯分離膜的制備和性能研究[D];東華大學;2017年

4 呂亞文;聚偏氟乙烯超濾膜改性及其抗污染性能的研究[D];北京工業(yè)大學;2001年

5 李欣;聚偏氟乙烯導熱性能改性研究[D];天津大學;2013年

6 何靜;聚偏氟乙烯荷電超濾膜的制備及性能研究[D];東北林業(yè)大學;2014年

本文編號：2051143