本文選題：硫酸氫銨 + 粉煤灰　； 參考：《有色金屬(冶煉部分)》2017年04期

【摘要】：通過X射線衍射分析了粉煤灰的物相結構,采用焙燒單因素試驗和正交試驗探索硫酸氫銨焙燒法提取粉煤灰中氧化鋁的工藝條件。結果表明,在硫酸氫銨與粉煤灰質量比為8.5∶1、焙燒溫度420℃、焙燒時間60min的條件下,氧化鋁的提取率可達84.5%。焙燒后熟料在下述最佳條件下氧化鋁的溶出率可達到95.9%:溶出溫度90℃,液固比8∶1,攪拌速率400r/min,溶出時間70min。
[Abstract]:The phase structure of fly ash is analyzed by X ray diffraction. The process conditions for extracting alumina in fly ash by roasting ammonium sulfate by roasting single factor test and orthogonal test are explored. The results show that the extraction rate of alumina is available under the condition of the mass ratio of ammonium hydrogen sulfate to fly ash is 8.5: 1, the calcination temperature is 420, and the calcination time is 60min. The dissolution rate of alumina can reach 95.9% under the following optimum conditions after 84.5%. calcination: the dissolution temperature is 90, the ratio of liquid to solid is 8: 1, the stirring rate is 400r/min, and the dissolution time is 70min.

【作者單位】： 沈陽醫(yī)學院化學系;東北大學冶金學院;
【基金】：國家自然科學基金資助項目(51204034)
【分類號】：TQ133.1

【相似文獻】

相關期刊論文 前10條

1 鄭宏;世界氧化鋁工業(yè)的進展[J];世界有色金屬;1996年11期

2 ;今年氧化鋁需求燒堿600萬噸[J];江蘇氯堿;2012年03期

3 ;氧化鋁及燒堿發(fā)展前景分析[J];江蘇氯堿;2012年06期

4 張寶琦,常崇緯;要大力發(fā)展我國氧化鋁工業(yè)[J];世界有色金屬;1997年09期

5 唐曉紅;王瑾;;氧化鋁的應用、項目風險與防范[J];價值工程;2012年04期

6 戴隆秀;段U_偉;汪燮卿;黃大智;李照非;;低碳烷氧基鋁水解制備氧化鋁的新方法[J];石油學報(石油加工);1994年04期

7 陳念貽;氧化鋁工業(yè)近年來的進步[J];化學世界;1954年08期

8 羅玉長,高學峰;氧化鋁水泥及其水化[J];輕金屬;2001年11期

9 陳燕玉;段先健;吳春蕾;杜海晶;;氣相氧化鋁的制備方法及應用前景[J];廣州化工;2014年14期

10 王永旺;松麗濤;郭昭華;池君洲;;高鋁粉煤灰提取氧化鋁技術綜述[J];煤炭工程;2013年04期

相關重要報紙文章 前3條

1 王祝堂;說說化學品氧化鋁[N];中國有色金屬報;2013年

2 記者 郁紅;今年氧化鋁需求燒堿600萬噸[N];中國化工報;2012年

3 孫立會;氧化鋁盲目投資令人擔憂[N];國際商報;2006年

，

本文編號：1811133