【摘要】：通過(guò)測(cè)試不同配合比鋼纖維活性粉末混凝土漿體的坍落擴(kuò)展度,研究微硅粉、礦渣粉以及鋼纖維摻量對(duì)漿體流動(dòng)性的影響。試驗(yàn)結(jié)果表明:鋼纖維活性粉末混凝土的漿體坍落擴(kuò)展度隨著微硅粉摻量的增加而降低,當(dāng)微硅粉摻量低于6%時(shí),其影響不明顯;其坍落擴(kuò)展度隨著礦渣粉摻量的增加而增大,礦渣粉摻量為15%時(shí)坍落擴(kuò)展度較未摻礦渣粉的RPC漿體提高9.2%;當(dāng)鋼纖維摻量為2.5%時(shí),漿體的流動(dòng)度達(dá)到理想狀態(tài)。
[Abstract]:By testing the collapsing and spreading degree of steel fiber reactive powder concrete paste with different mix ratio, the microsilica powder was studied. The effect of slag powder and steel fiber content on slurry fluidity. The experimental results show that the slurry collapse propagation degree of steel fiber reactive powder concrete decreases with the increase of the content of micro-silica powder, but the effect is not obvious when the content of micro-silica powder is lower than 6. With the increase of slag powder content, the collapse expansion degree of RPC slurry increases by 9.2, and when the slag powder content is 15, the fluidity of slurry reaches the ideal state when the content of steel fiber is 2.5.
【作者單位】： 上海交通大學(xué)船舶海洋與建筑工程學(xué)院;中國(guó)聯(lián)合工程公司;
【基金】：國(guó)家自然科學(xué)基金項(xiàng)目(51178264) 鐵道部科技研究開(kāi)發(fā)計(jì)劃項(xiàng)目(J2011G003)
【分類(lèi)號(hào)】：TU528

【相似文獻(xiàn)】

相關(guān)期刊論文 前10條

1 歐陽(yáng)幼玲;陳迅捷;陸采榮;方t，

本文編號(hào)：1647456